Generic Nylon 66 - Glass Bead
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 24czeF_Generic-Nylon-66---Glass-Bead.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Nylon 66 - Glass Bead This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.23 - 1.48 | g/cm³ | ASTM D792 |
| 23°C | 1.22 - 1.49 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (275°C/0.325 kg) | 1.0 - 4.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.34 - 2.1 | % | ASTM D955 |
| Transverse flow : 23°C | 1.4 - 2.0 | % | ASTM D955 |
| 23°C | 0.47 - 1.7 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.66 - 1.0 | % | ASTM D570 |
| 23°C, 24 hr | 0.68 - 1.2 | % | ISO 62 |
| Saturated, 23°C | 4.5 - 7.1 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.51 - 2.5 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 119 - 122 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 2800 - 6760 | MPa | ASTM D638 |
| 23°C | 3590 - 5440 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 75.1 - 138 | MPa | ASTM D638 |
| Yield, 23°C | 61.9 - 112 | MPa | ISO 527-2 |
| Fracture, 23°C | 53.8 - 105 | MPa | ASTM D638 |
| Fracture, 23°C | 55.3 - 95.8 | MPa | ISO 527-2 |
| 23°C | 53.7 - 140 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 2.4 - 4.7 | % | ASTM D638 |
| Yield, 23°C | 1.7 - 4.4 | % | ISO 527-2 |
| Fracture, 23°C | 1.7 - 9.0 | % | ASTM D638 |
| Fracture, 23°C | 1.5 - 9.3 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 3260 - 6960 | MPa | ASTM D790 |
| 23°C | 3150 - 4720 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 98.5 - 166 | MPa | ASTM D790 |
| 23°C | 99.0 - 187 | MPa | ISO 178 |
| Yield, 23°C | 103 - 124 | MPa | ASTM D790 |
| Fracture, 23°C | 128 - 189 | MPa | ASTM D790 |
| Compressive Strength (23°C) | 47.6 - 252 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 1.5 - 7.7 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 19 - 42 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 31 - 55 | J/m | ASTM D256 |
| 23°C | 2.0 - 6.3 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 200 - 640 | J/m | ASTM D256 |
| 23°C | 20 - 40 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 204 - 260 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 198 - 256 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 65.6 - 254 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 74.3 - 250 | °C | ISO 75-2/A |
| Continuous Use Temperature | 90.0 - 121 | °C | ASTM D794 |
| Vicat Softening Temperature | 200 - 255 | °C | ISO 306 |
| Melting Temperature | |||
| -- | 255 - 260 | °C | |
| -- | 256 - 263 | °C | ISO 11357-3 |
| -- | 256 - 260 | °C | ASTM D3418 |
| -- | 260 | °C | ISO 3146 |
| Linear thermal expansion coefficient | |||
| Flow | 5.9E-5 - 6.1E-5 | cm/cm/°C | ASTM D696 |
| Flow | 3.0E-5 - 7.1E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 3.0E-5 - 6.1E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity (23°C) | 0.26 - 0.36 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+4 - 1.3E+14 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 1.0E+11 - 1.0E+15 | ohms·cm | ASTM D257 |
| 23°C | 1.0E+12 - 2.5E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 23°C | 16 - 30 | kV/mm | ASTM D149 |
| 23°C | 29 - 41 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 23°C | 3.70 - 4.20 | ASTM D150 | |
| 23°C | 3.79 | IEC 60250 | |
| Dissipation Factor | |||
| 23°C | 0.014 - 0.016 | ASTM D150 | |
| 23°C | 1.0E-4 - 0.020 | IEC 60250 | |
| Comparative Tracking Index | 399 - 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index | 650 - 658 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 650 - 655 | °C | IEC 60695-2-13 |
| Oxygen Index | 23 - 27 | % | ASTM D2863, ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.0 - 83.0 | °C | |
| Drying Time | 2.8 - 5.3 | hr | |
| Suggested Max Moisture | 0.12 - 0.20 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 265 - 300 | °C | |
| Middle Temperature | 269 - 295 | °C | |
| Front Temperature | 280 - 300 | °C | |
| Nozzle Temperature | 260 - 290 | °C | |
| Processing (Melt) Temp | 274 - 294 | °C | |
| Mold Temperature | 73.5 - 102 | °C | |
| Injection Pressure | 86.1 - 104 | MPa | |
| Holding Pressure | 46.8 - 60.2 | MPa | |
| Back Pressure | 0.258 - 0.518 | MPa | |
| Screw Speed | 45 - 91 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Nylon 66 - Glass BeadThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom SA5007 | Spartech Polycom | ABS | Spartech |
| Sumitomo Phenolic FM 21386 | Sumitomo Bakelite North America, Inc. | Phenolic | Sumitomo Phenolic |
| Lutene® MB9205 | LG Chem Ltd. | LDPE | Lutene® |
| MARPOL® EVA 1707 | Marco Polo International, Inc. | EVA | MARPOL® EVA |
| Sylvin 5145-85 Clear Yellow 4112 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |