Sunny® ASA EB100
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | Guangdong Shunde Shunyan New Material Co., Ltd. |
| Trademark: | Sunny® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 24Ar3P_Sunny-ASA-EB100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EP Acrylonitrile Styrene acrylate copolymer |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- 1 | 1.05 | g/cm³ | ASTM D792 |
| 23°C | 1.05 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.40 to 0.70 | % | ASTM D955 |
| 23°C | 0.40 to 0.70 | % | ISO 294-4 |
| Water Absorption | |||
| Equilibrium, 23°C | 0.90 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.90 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- 2 | 50.0 | MPa | ASTM D638 |
| -- | 50.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 45 | % | ASTM D638 |
| Break | 50 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span | 1160 | MPa | ASTM D790 |
| 50.0 mm Span | 1200 | MPa | ISO 178 |
| Flexural Strength | |||
| 50.0 mm Span | 78.0 | MPa | ASTM D790 |
| -- 4 | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 130 | J/m | ASTM D256 |
| 23°C | 12 | kJ/m² | ISO 180/1A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 105 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 225 | °C | |
| Middle Temperature | 210 | °C | |
| Front Temperature | 190 | °C | |
| Processing (Melt) Temp | 200 | °C | |
| Mold Temperature | 80.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 50 mm span |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NILENE® E3 | Taro Plast S.p.A. | PP Copolymer | NILENE® |
| Bluestar Epoxy EX-13 | Bluestar New Chemical Materials Co. Ltd | Epoxy | Bluestar Epoxy |
| Clariant PBT PBT-1300G25 | Clariant Corporation | PBT | Clariant PBT |
| LNP™ LUBRICOMP™ Lexan_WR2210 compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ LUBRICOMP™ |
| LNP™ THERMOCOMP™ KF002L compound | SABIC Innovative Plastics | Acetal (POM) Homopolymer | LNP™ THERMOCOMP™ |