Generic Acetal (POM) Copolymer - Glass Bead
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 23TXgb_Generic-Acetal-POM-Copolymer---Glass-Bead.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Acetal (POM) Copolymer - Glass Bead This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.47 - 1.70 | g/cm³ | ASTM D792 |
| 23°C | 1.47 - 1.64 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 5.0 - 22 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 3.80 - 17.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.47 - 2.5 | % | ASTM D955 |
| 23°C | 1.3 - 2.0 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.19 - 0.50 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.16 - 0.80 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 75 - 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 2000 - 7050 | MPa | ASTM D638 |
| 23°C | 2980 - 4100 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Yield, 23°C | 35.0 - 50.0 | MPa | ISO 527-2 |
| Fracture, 23°C | 37.0 - 60.0 | MPa | ISO 527-2 |
| 23°C | 35.8 - 82.8 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 8.1 - 10 | % | ASTM D638 |
| Yield, 23°C | 4.0 - 8.0 | % | ISO 527-2 |
| Fracture, 23°C | 1.5 - 16 | % | ASTM D638 |
| Fracture, 23°C | 4.8 - 20 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 2470 - 4170 | MPa | ASTM D790 |
| 23°C | 1900 - 4900 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 55.2 - 103 | MPa | ASTM D790 |
| 23°C | 60.0 - 110 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.0 - 4.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 20 - 60 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 29 - 58 | J/m | ASTM D256 |
| 23°C | 2.9 - 6.0 | kJ/m² | ISO 180 |
| Unnotched Izod Impact (23°C) | 310 - 550 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 160 - 163 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 102 - 161 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 93.5 - 125 | °C | ISO 75-2/A |
| Melting Temperature | |||
| -- | 166 | °C | |
| -- | 165 - 167 | °C | ISO 11357-3 |
| CLTE - Flow | 6.3E-5 - 8.1E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 1.0E+15 - 1.0E+16 | ohms | ASTM D257 |
| -- | 1.0E+13 - 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+14 - 3.5E+14 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | |||
| 23°C | 18 - 19 | kV/mm | ASTM D149 |
| 23°C | 20 - 40 | kV/mm | IEC 60243-1 |
| Dissipation Factor (23°C) | 6.0E-3 - 0.030 | IEC 60250 | |
| Comparative Tracking Index | 598 - 600 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 81.5 - 121 | °C | |
| Drying Time | 2.0 - 3.5 | hr | |
| Suggested Max Moisture | 0.10 - 0.15 | % | |
| Suggested Max Regrind | 15 | % | |
| Rear Temperature | 175 - 200 | °C | |
| Middle Temperature | 184 - 200 | °C | |
| Front Temperature | 195 - 216 | °C | |
| Nozzle Temperature | 191 - 200 | °C | |
| Processing (Melt) Temp | 200 - 208 | °C | |
| Mold Temperature | 79.3 - 107 | °C | |
| Injection Pressure | 85.3 - 121 | MPa | |
| Back Pressure | 0.250 - 1.05 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Acetal (POM) Copolymer - Glass BeadThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Retpol® 1210 TF HS UV3 | PolyPacific Pty. Ltd. | PP Copolymer | Retpol® |
| TRANSMARE® 14CNF30-0.001 | Transmare Compounding B.V. | PP Copolymer | TRANSMARE® |
| Akulon® S223-F | DSM Engineering Plastics | Nylon 66 | Akulon® |
| Andur 9500 AP/Curene® 442 | Anderson Development Company | PUR-Ether/TDI | Andur |
| Sylvin 8707-80 Brown 7463 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |