Ultramid® TG3S BK-104
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 23IHgw_Ultramid-TG3S-BK-104.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid TG3S BK-104 is a 15% glass reinforced, heat stabilized, impact modified PA6 injection molding compound developed for applications requiring improved toughness in combination with a balance of strength, stiffness, excellent moldability and surface aesthetics. Applications It is generally recommended for application such as window hardware, wheel chairs wheels, bicycle wheels, power tool housings, hose clamps, clips and fasteners. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.21 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 4600 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 90.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 3.5 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 4390 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 13 | kJ/m² | ISO 179 |
| Notched Izod Impact Strength | ISO 180 | ||
| -40°C | 5.4 | kJ/m² | |
| 23°C | 17 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 211 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 180 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | °C | ISO 3146 |
| RTI Elec | UL 746 | ||
| 1.00 mm | 65.0 | °C | |
| 1.50 mm | 65.0 | °C | |
| 3.00 mm | 65.0 | °C | |
| RTI Imp | UL 746 | ||
| 1.00 mm | 65.0 | °C | |
| 1.50 mm | 65.0 | °C | |
| 3.00 mm | 65.0 | °C | |
| RTI Str | UL 746 | ||
| 1.00 mm | 65.0 | °C | |
| 1.50 mm | 65.0 | °C | |
| 3.00 mm | 65.0 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.00 mm | HB | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.080 | % | |
| Rear Temperature | 245 to 275 | °C | |
| Middle Temperature | 260 to 285 | °C | |
| Front Temperature | 270 to 295 | °C | |
| Nozzle Temperature | 270 to 295 | °C | |
| Processing (Melt) Temp | 270 to 295 | °C | |
| Mold Temperature | 80.0 to 95.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ROPOTEN® OV-03-110 | LUKOIL Bulgaria Ltd. | LDPE | ROPOTEN® |
| Unipren® Elastomers A3 NTLA010 35A EB06S1 UP329 | Petropol Industry and Trade of Polymers LTDA | TPE | Unipren® Elastomers |
| BCC Resins BC 8001 | BCC Products Inc. | PUR, Unspecified | BCC Resins |
| Bluestar Epoxy EX-17D | Bluestar New Chemical Materials Co. Ltd | Epoxy | Bluestar Epoxy |
| LIHAN® T9706EP | Nanjing Lihan Chemical Co., Ltd. | PBT | LIHAN® |