SABIC® PPcompound 7890A
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 22gpQY_SABIC-PPcompound-7890A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PPcompound 7890A is a mineral filled modified polypropylene.This material combines a very high flow with a good scratch resistance, anti static properties, low density and a good stiffness. This material has a very broad processing window and good esthical performance. Typical applications include esthetical automotive interior parts such as door panels and interior trim. SABIC® PPcompound 7890A is a designated automotive grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.960 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 25 | g/10 min | ISO 1133 |
| Molding Shrinkage (24 hr) | 1.0 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Injection Molded) | 66 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/1A/50 | ||
| Yield, Injection Molded | 24.0 | MPa | |
| Break, Injection Molded | 18.0 | MPa | |
| Tensile Strain (Break, Injection Molded) | 20 | % | ISO 527-2/1A/50 |
| Flexural Modulus 1(Injection Molded) | 1800 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | 7.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (-40°C, Injection Molded) | 40 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | ISO 180/4A | ||
| -20°C, Injection Molded | 4.0 | kJ/m² | |
| 0°C, Injection Molded | 5.0 | kJ/m² | |
| 23°C, Injection Molded | 7.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 105 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 130 | °C | ISO 306/A |
| CLTE - Flow | ASTM D696 | ||
| -30 to 30°C | 8.0E-5 | cm/cm/°C | |
| 23 to 80°C | 1.1E-4 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | Method I (3 point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP 570P | SABIC Americas, Inc. | PP Homopolymer | SABIC® PP |
| 4LAC® 25H30000 | 4Plas | ABS | 4LAC® |
| Nypol® PA A1 G30 PRTA011 NR105 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Caltex PP RE72 | GS Caltex | TPO | Caltex PP |
| CP PRYME® Polycarbonate PC100RULUV-18M BT Clear | Chase Plastics Services Inc. | PC | CP PRYME® Polycarbonate |