REPOL® H110MA
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Reliance Industries Limited |
| Trademark: | REPOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 22ehtU_REPOL-H110MA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Repol H110MA is recommended for Injection Moulding processes. Repol H110MA is an ideal choice for moulding rigid containers, thermowares and housewares. It is also suitable as a compounding base and blending material in furniture compound. Repol H110MA contains antistat agent that reduces static charge build-up in products. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 11 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, Injection Molded) | 36.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Yield, Injection Molded) | 10 | % | ASTM D638 |
| Flexural Modulus - 1% Secant (Injection Molded) | 1650 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, Injection Molded) | 27 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 104 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type I, 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsamid® AZM 30 Noir T6LD | Arkema | Nylon 12 | Rilsamid® |
| RTP 202 Z | RTP Company | Nylon 66 | RTP |
| NANCAR® 4155J | Nantex Industry Co., Ltd. | NBR | NANCAR® |
| ACCUTECH™ CP0436G25M5CL | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| Osterlene® LDC1821 | Osterman & Company | LDPE | Osterlene® |