VALOX™ PDR4922 resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 22T1qu_VALOX-PDR4922-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GF filled PBT grade |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 13 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 12.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.16 | % | |
| Across Flow : 3.20 mm | 0.94 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.030 | % | |
| Equilibrium, 23°C, 50% RH | 0.030 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 5410 | MPa | ASTM D638 |
| -- | 5230 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 85.0 | MPa | ASTM D638 |
| Yield | 85.0 | MPa | ISO 527-2/50 |
| Break 3 | 81.0 | MPa | ASTM D638 |
| Break | 81.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 2.4 | % | ASTM D638 |
| Yield | 3.0 | % | ISO 527-2/50 |
| Break 5 | 3.3 | % | ASTM D638 |
| Break | 3.6 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 4580 | MPa | ASTM D790 |
| -- 7 | 4870 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 130 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 133 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 58 | J/m | ASTM D256 |
| 23°C | 100 | J/m | ASTM D256 |
| -30°C 10 | 6.0 | kJ/m² | ISO 180/1A |
| 23°C 11 | 11 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 8.80 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 216 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 184 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 170 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 200 | °C | ASTM D1525 13 |
| -- | 195 | °C | ISO 306/B50 |
| -- | 196 | °C | ISO 306/B120 |
| CLTE | |||
| Flow : -40 to 40°C | 4.2E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 4.4E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 1.1E-4 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 12 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 80 | % | |
| Rear Temperature | 238 to 254 | °C | |
| Middle Temperature | 243 to 260 | °C | |
| Front Temperature | 249 to 266 | °C | |
| Nozzle Temperature | 243 to 260 | °C | |
| Processing (Melt) Temp | 249 to 266 | °C | |
| Mold Temperature | 48.9 to 76.7 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 50 to 100 | rpm | |
| Vent Depth | 0.025 to 0.038 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® GF25-60 XE-NBK1 | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| GAPEX® RPP25EA32BL | Ferro Corporation | PP Homopolymer | GAPEX® |
| En Chuan 6123TA | En Chuan Chemical Industries Co,. Ltd. | Polyester, TS | En Chuan |
| LNP™ LUBRICOMP™ RX05050 compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ LUBRICOMP™ |
| OmniLon™ PA6/6 GR43 FR All Colors | OMNI Plastics, LLC | Nylon 66 | OmniLon™ |