Lustran® ABS PG298
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Styrolution |
| Trademark: | Lustran® ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 22Ni8R_Lustran-ABS-PG298.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lustran ABS PG 298 resin is a plateable grade of ABS (acrylonitrile butadiene styrene) for use in automotive and general-purpose applications. This injection molding grade was designed specifically for improved thermocycle performance and outstanding plate adhesion. It provides a unique combination of flow and rigidity, with increased scratch resistance and increased resistance to deformation on plating racks. The resin is available in gray color only. Lustran ABS PG 298 resin is used in the automotive industry for plated grilles, wheel covers, exterior mirror housings, and exterior trim. It is also used for decorative parts in the appliance and lawn and garden markets. As with any product, use of Lustran ABS PG 298 resin in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Specific Volume | 0.940 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 220°C/10.0 kg | 19 | g/10 min | ASTM D1238 |
| 230°C/3.8 kg | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 - 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ASTM D638 | ||
| -- 1 | 7580 | MPa | ASTM D638 |
| -- 2 | 2770 | MPa | ASTM D638 |
| Tensile Strength | |||
| Yield | 40.0 | MPa | ASTM D638 |
| Yield | 43.0 | MPa | ISO 527-2 |
| Flexural Modulus | |||
| -- 3 | 12500 | MPa | ASTM D790 |
| -- 4 | 2830 | MPa | ASTM D790 |
| -- | 2730 | MPa | ISO 178 |
| Flexural Strength | ASTM D790 | ||
| Yield 5 | 117 | MPa | ASTM D790 |
| Yield 6 | 78.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 170 | J/m | ASTM D256 |
| -40°C 7 | 6.4 | kJ/m² | ISO 180/1A |
| 23°C 8 | 14 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.18mm | 91.1 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 12.7mm, molded | 103 | °C | ASTM D648 |
| 0.45 MPa, annealed, 12.7mm | 100 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.18mm | 83.9 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 12.7mm, molded | 98.3 | °C | ASTM D648 |
| 1.8 MPa, annealed, 12.7mm | 97.2 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 110 | °C | ASTM D1525 9 |
| -- | 36.6 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 10(2.01 mm) | 48 | mm/min | SAE J1685 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| A | 82.2 - 87.8 | °C | |
| B | 71.1 - 76.7 | °C | |
| Drying Time | |||
| A | 2.0 | hr | |
| B | 4.0 | hr | |
| Suggested Max Moisture | < 0.10 | % | |
| Suggested Shot Size | 50 - 75 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 243 - 252 | °C | |
| Middle Temperature | 249 - 257 | °C | |
| Front Temperature | 254 - 263 | °C | |
| Nozzle Temperature | 254 - 263 | °C | |
| Processing (Melt) Temp | 260 - 277 | °C | |
| Mold Temperature | 48.9 - 60.0 | °C | |
| Injection Pressure | 68.9 - 110 | MPa | |
| Injection Rate | Slow | ||
| Back Pressure | 0.345 - 0.689 | MPa | |
| Clamp Tonnage | 2.8 - 5.5 | kN/cm² | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.5:1.0 |
| Injection instructions |
|---|
| Hold Pressure: 50 to 75% of Injection PressureScrew Speed: Moderate |
| Note Message | |
|---|---|
| 1 . | Plated |
| 2 . | Unplated |
| 3 . | Plated |
| 4 . | Unplated |
| 5 . | Plated |
| 6 . | Unplated |
| 7 . | 4x10 mm bar |
| 8 . | 4x10 mm bar |
| 9 . | 标准 B (120°C/h), 压 力1 (10N) |
| 10 . | 2x100x355 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UMG ALLOY® TC-6F | UMG ABS, Ltd. | PC+ABS | UMG ALLOY® |
| NaturePlast PBE 001 | NaturePlast | Polyester, TP | NaturePlast |
| Network Polymers PP PPR 20 1201 CAS | Network Polymers, Inc. | PP Random Copolymer | Network Polymers PP |
| EPO-TEK® H67-MP | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Rotuba CAB B9086 (10% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |