Dynacom 702
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Dynachem Co. Ltd. |
| Trademark: | Dynacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 20HvVg_Dynacom-702.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Dynacom 702 is a Polypropylene Copolymer (PP Copolymer) material. It is available in Asia Pacific. Primary attribute of Dynacom 702: Flame Rated. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.960 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 22 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow 1 | 1.4 to 1.5 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | < 0.020 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 112 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | 39.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 20 | % | ASTM D638 |
| Flexural Modulus 4 | 2150 | MPa | ASTM D790 |
| Flexural Strength 5 | 49.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 23 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 130 | °C | ASTM D648 |
| Vicat Softening Temperature | 157 | °C | ASTM D1525 6 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.00 mm) | 40 | kV/mm | ASTM D149 |
| Arc Resistance | 70.0 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-2 | UL 94 |
| Note Message | |
|---|---|
| 1 . | Thickness: 2 to 3 mm |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 3.0 mm/min |
| 5 . | 3.0 mm/min |
| 6 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® mLLF 804 | Marco Polo International, Inc. | mLLDPE | MARPOL® |
| Starflam PF0057E | Eurostar Engineering Plastics | Nylon 6 | Starflam |
| THERMOLAST® K TF4CGT (Series: FC) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Hax™ HFC 0108/4 | Fainplast Compounds S.r.l | Polyolefin, Unspecified | Hax™ |
| POLYCOMPO PE ACE30N | POLYCOMPO Co.,Ltd. | LDPE | POLYCOMPO PE |