Order Products : sales@su-jiao.com
MARPOL® HDB 503G
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Marco Polo International, Inc. |
| Trademark: | MARPOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1zzLd4_MARPOLHDB503G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MARPOL® HDB 503G is a high density polyethylene, gas phase blow molding resin. It features an excellent balance of physical and molding properties. Recommended Applications: Industrial chemical bottles, household chemical bottles, automotive fluid bottles, toys and pharmaceutical bottles. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.954 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.33 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (100% Igepal) | 70.0 | hr | ASTM D1693B |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 27.2 | MPa | ASTM D638 |
| Fracture | 31.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 7.0 | % | ASTM D638 |
| Fracture | 950 | % | ASTM D638 |
| Flexural Modulus | 1140 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 140 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 125 | °C | ASTM D1525 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stratasys PC-ABS | Stratasys | PC+ABS | Stratasys |
| Ultramid® B36 01 | BASF Corporation | Nylon 6 | Ultramid® |
| Laprene® 830000951 | SO.F.TER. SPA | SEBS | Laprene® |
| Sylvin 3280-85 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ THERMOCOMP™ AF003 compound | SABIC Innovative Plastics | ABS | LNP™ THERMOCOMP™ |