Zytel® HTN FR55G50NHLW NC010
| Category: | PPA , HIGH PERFORMANCE POLYAMIDE RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® HTN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1zGuwi_ZytelHTNFR55G50NHLWNC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 50% Glass Reinforced, Flame Retardant, Non-Halogenated, PPA, High Performance Polyamide with Low Warpage Characteristics |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Part Marking Code (ISO 11469) |
|
| Part Marking Code (SAE J1344) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.65 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 0.20 | % | ISO 294-4 |
| Flow | 0.10 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 18000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 200 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.6 | % | ISO 527-2 |
| Flexural Modulus | 16600 | MPa | ISO 178 |
| Flexural Stress | 305 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 217 | °C | ISO 75-2/A |
| Melting Temperature 1 | 298 | °C | ISO 11357-3 |
| RTI Elec | UL 746 | ||
| 0.40 mm | 65.0 | °C | UL 746 |
| 0.75 mm | 65.0 | °C | UL 746 |
| 1.5 mm | 65.0 | °C | UL 746 |
| 3.0 mm | 65.0 | °C | UL 746 |
| RTI Imp | UL 746 | ||
| 0.40 mm | 65.0 | °C | UL 746 |
| 0.75 mm | 65.0 | °C | UL 746 |
| 1.5 mm | 65.0 | °C | UL 746 |
| 3.0 mm | 65.0 | °C | UL 746 |
| RTI | UL 746 | ||
| 0.40 mm | 65.0 | °C | UL 746 |
| 0.75 mm | 65.0 | °C | UL 746 |
| 1.5 mm | 65.0 | °C | UL 746 |
| 3.0 mm | 65.0 | °C | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 2(1.00 mm) | < 100 | mm/min | ISO 3795 |
| Flame Rating | UL 94, IEC 60695-11-10, -20 | ||
| 0.75 mm | V-0 | UL 94, IEC 60695-11-10, -20 | |
| 1.5 mm | V-0 | UL 94, IEC 60695-11-10, -20 | |
| FMVSS Flammability | B | FMVSS 302 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Recommended | yes | ||
| Drying Temperature | 100 | °C | |
| Drying Time - Desiccant Dryer | 6.0 - 8.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Processing (Melt) Temp | 300 - 315 | °C | |
| Mold Temperature | 70 - 130 | °C |
| Note Message | |
|---|---|
| 1 . | First Heat |
| 2 . | FMVSS 302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRIREX® 3020PJ | Samyang Corporation | PC | TRIREX® |
| Aaroprene® CFIPP 2010 | Aaron Industries Corp. | PP, Unspecified | Aaroprene® |
| Latilub 66-10T Y/15 | LATI S.p.A. | Nylon 66 | Latilub |
| Monprene® RG-20170 (PRELIMINARY DATA) | Teknor Apex Company | TPE | Monprene® |
| Durethan® AM 40 X H2.0 DUS041 901510 | LANXESS GmbH | Nylon 66 | Durethan® |