P-FLEX 020
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Putsch Kunststoffe GmbH |
| Trademark: | P-FLEX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1ywoQp_P-FLEX-020.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High impact ABS with good flexibility. |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 10 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.70 - 0.90 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 37.0 | MPa | ISO 527-2 |
| Fracture | 36.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 10 | % | ISO 527-2 |
| Flexural Modulus | 2200 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180 | ||
| -20°C | 10 | kJ/m² | ISO 180 |
| 23°C | 28 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 96.0 | °C | ISO 306/B |
| Additional Information |
|---|
| Tensile Strength, ISO 527: 37 MPaBurn Rate, MVS 302: 12 mm |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 240 - 260 | °C | |
| Mold Temperature | 30.0 - 40.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rainmaker Polypropylene MCCPGL40 | Rainmaker Polymers LLC | PP Copolymer | Rainmaker Polypropylene |
| Spartech Polycom SP7015 | Spartech Polycom | PC | Spartech |
| TOTAL Polypropylene PPH 10060 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| Braskem PE GP5550 | Braskem | HDPE | Braskem PE |
| PENTAMID B E20 H natur | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |