POCAN® BF 4222 000000
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | LANXESS Corporation |
| Trademark: | POCAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1ygARb_POCAN-BF-4222-000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT, 20 % glass fibers, injection molding, flame retardant |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.57 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 12.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 260°C, 2.00 mm 1 | 1.1 | % | |
| Across Flow : 120°C, 2 hr, 2.00 mm 2 | 0.20 | % | |
| Flow : 260°C, 2.00 mm 3 | 0.50 | % | |
| Flow : 120°C, 2 hr, 2.00 mm 4 | 0.20 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.40 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 176 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 7500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break, 23°C | 2.60 | MPa | ASTM D638 |
| Break, 23°C | 115 | MPa | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 7900 | MPa | ISO 178/A |
| Flexural Stress 6(23°C) | 190 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 7(23°C) | 3.3 | % |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Shortname | PBT, GFHMR, 09-070, GF20 | ISO 7792 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.0 to 0.020 | % | Karl Fisher |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | < 10 | kJ/m² | |
| 23°C | < 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 45 | kJ/m² | |
| 23°C | 50 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | < 10 | kJ/m² | |
| 23°C | < 10 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 40 | kJ/m² | |
| 23°C | 45 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 215 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 195 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 211 | °C | ISO 306/B50 |
| Ball Pressure Test (211°C) | Pass | IEC 60695-10-2 | |
| Melting Temperature 8 | 222 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 3.0E-5 | cm/cm/°C | |
| Transverse : 23 to 55°C | 1.0E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+17 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | > 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength (23°C, 1.00 mm) | 31 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.750 mm | 960 | °C | |
| 1.50 mm | 960 | °C | |
| 3.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.750 mm | 800 | °C | |
| 1.50 mm | 800 | °C | |
| 3.00 mm | 800 | °C | |
| Oxygen Index 9 | 29 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 120 | °C | |
| Drying Time - Dry Air Dryer | 4.0 to 8.0 | hr | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2; MT 80°C; 600 Bar |
| 2 . | 60x60x2 |
| 3 . | 60x60x2; MT 80°C; 600 Bar |
| 4 . | 60x60x2 |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| 9 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polylink Polymer PP 411-401 (CL) | Polylink Polymers (India) Ltd. | XLPE | Polylink Polymer |
| TEREZ PA 6 7500 TF 20 N | TER HELL PLASTIC GMBH | Nylon 6 | TEREZ PA 6 |
| Jampilen RP210M | Jam Polypropylene Company | PP Random Copolymer | Jampilen |
| LNP™ LUBRILOY™ RX05497 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRILOY™ |
| MAXAMID™ EPDMRC036-HSL-BK09 | Pier One Polymers, Inc. | Nylon 6 | MAXAMID™ |