| 10% CARBON FIBER FILLED POLYSULFONE |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 to 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 96.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 to 3.0 | % | ASTM D638 |
| Flexural Modulus | 6890 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 96 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 182 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+6 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 135 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 327 to 371 | °C | |
| Middle Temperature | 327 to 371 | °C | |
| Front Temperature | 327 to 371 | °C | |
| Processing (Melt) Temp | 338 to 349 | °C | |
| Mold Temperature | 149 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.038 to 0.076 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nipol® SBR NS310S | Zeon Corporation | SBR, Solution | Nipol® SBR |
| Nucrel® 30907 | DuPont Packaging & Industrial Polymers | EAA | Nucrel® |
| NYCOA Polyamide 851 | Nycoa (Nylon Corporation of America) | Nylon 6 | NYCOA Polyamide |
| Hytrel® 21UV | DuPont Performance Polymers | TPC-ET | Hytrel® |
| Lion Idemitsu Composites PPS NT-783 | Lion Idemitsu Composites Co., Ltd. | PPS | Lion Idemitsu Composites PPS |