| High Tg version of EPO-TEK®353ND with low modulus and good toughness. Replacement for EPO-TEK® 364. Complies with USP Class VI biocompatibility standards. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature 1 | > 140 | °C | |
| CLTE - Flow | |||
| -- 2 | 4.5E-5 | cm/cm/°C | |
| -- 3 | 1.9E-4 | cm/cm/°C |
| Optical | Nominal Value | Unit | |
|---|---|---|---|
| Refractive Index 4 | 1.573 | ||
| Transmittance | |||
| 600 nm | 69.0 | % | |
| 800 to 1640 nm | > 98.0 | % |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 20 | ||
| Part B | Mix Ratio by Weight: 1.0 | ||
| Shelf Life (23°C) | 52 | wk |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Degradation Temperature | 443 | °C | |
| Die Shear Strength - >10 kg (23°C) | 23.4 | MPa | |
| Operating Temperature | |||
| Continuous | -55 to 225 | °C | |
| Intermittent | -55 to 325 | °C | |
| Storage Modulus | 1.82 | GPa | |
| Weight Loss on Heating | |||
| 200°C | < 0.050 | % | |
| 250°C | < 0.050 | % | |
| 300°C | < 0.050 | % |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Color | |||
| -- 5 | Amber | ||
| -- 6 | White | ||
| Density | |||
| Part B | 1.02 | g/cm³ | |
| Part A | 1.20 | g/cm³ | |
| Viscosity 7(23°C) | 24 to 42 | Pa·s | |
| Curing Time (150°C) | 1.0 | hr | |
| Pot Life | 240 | min |
| Cured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Shore Hardness (Shore D) | 69 | ||
| Lap Shear Strength (23°C) | 10.8 | MPa | |
| Relative Permittivity (1 kHz) | 2.83 | ||
| Volume Resistivity (23°C) | > 2.0E+12 | ohms·cm | |
| Dissipation Factor (1 kHz) | 0.011 |
| Note Message | |
|---|---|
| 1 . | Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-200°C @ 20°C/Min |
| 2 . | Below Tg |
| 3 . | Above Tg |
| 4 . | 589 nm |
| 5 . | Part B |
| 6 . | Part A |
| 7 . | 2.5 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVAMID® 66 GF 40 E/2M | Plastcom | Nylon 66 | SLOVAMID® 66 |
| Sunny® PPS 1150 | Guangdong Shunde Shunyan New Material Co., Ltd. | PPS | Sunny® |
| Celcon® WR90Z | Celanese Corporation | Acetal (POM) Copolymer | Celcon® |
| Daelim Po1y® LH-6070 | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| Hyundai EP PPC HP908 | HYUNDAI EP Co., Ltd. | PP Copolymer | Hyundai EP PPC |