Bergamid™ B70 VN4805 LS PM-Z BK
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Bergamid™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1xmcgf_Bergamid-B70-VN4805-LS-PM-Z-BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 6013041 |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density 1(23°C) | 1.07 | 1.07 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 2(23°C, 4.00 mm) | 2.0 | -- | % | ISO 294-4 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C, 4.00 mm, Injection Molded) | 2000 | 1050 | MPa | ISO 527-2/50 |
| Tensile Stress (Yield, 23°C, 4.00 mm, Injection Molded) | 43.0 | 28.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | |||
| Yield, 23°C, 4.00 mm | 3.0 | 4.0 | % | |
| Break, 23°C, 4.00 mm, Injection Molded | > 80 | > 150 | % | |
| Flexural Modulus (23°C, Injection Molded) | 1200 | 450 | MPa | ISO 178 |
| Flexural Stress (23°C, Injection Molded) | 42.0 | 13.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | 89 | 93 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C, Injection Molded | No Break | No Break | ||
| 23°C, Injection Molded | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Vicat Softening Temperature | 165 | -- | °C | ISO 306/B |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+15 | 1.0E+15 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+15 | 1.0E+15 | ohms·cm | ASTM D257 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (3.20 mm, ALL) | HB | HB | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | ±0.02 |
| 2 . | Bergmann method |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKAFIN™ PB50FR | Mando Advanced Materials Co., Ltd. | PP, Unspecified | TEKAFIN™ |
| Addisil™ 462 E | Momentive Performance Materials Inc. | Rubber | Addisil™ |
| DURACON® MS-02 | Polyplastics Co., Ltd. | Acetal (POM) Copolymer | DURACON® |
| ELASTOSIL® LR 6239 F | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| Petrothene® LB560201 | LyondellBasell Industries | HDPE | Petrothene® |