LNP™ LUBRICOMP™ RX94033 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1x6pzn_LNP-LUBRICOMP-RX94033-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP LUBRICOMP RX94033 is a compound based on PA 66 resin containing Aramide Fiber, Glass Fiber, PTFE. Added features include: Internally Lubricated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.35 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.81 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6300 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 117 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.8 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 5300 | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | ||
| -- 3 | 168 | MPa | |
| -- 4 | 167 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 5(23°C) | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 6(23°C) | 45 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 7 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 255 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 232 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 4.2E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 1.0E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 277 to 288 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Yield |
| 4 . | Break |
| 5 . | 80*10*4 |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SILVER® PC2320.F | Guangdong Silver Age Sci & Tech. Co., Ltd | PC | SILVER® |
| BCC Resins BC 6004 | BCC Products Inc. | Epoxy | BCC Resins |
| Amilan® HF3064G30 | Toray Resin Company | Nylon 66 | Amilan® |
| APEX® 90-A482R-65-NT | Teknor Apex Company | PVC, Flexible | APEX® |
| Eco-Solutions GP335-13 | MINIMA Technoloy Co. Ltd. | Biodeg Polymers | Eco-Solutions |