TOTAL Polystyrene Compound 9217
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polystyrene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1x4fMB_TOTAL-Polystyrene-Compound-9217.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polystyrene Compound 9217S a super impact polystyrene alloy with high level of stress crack resistance. It has excellent mechanical properties and good abrasion and tear resistance. Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.00 | g/cm³ | ASTM D792 |
| Apparent Density | 0.60 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 5.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow | 0.40 - 0.70 | % | ASTM D955 |
| Water Absorption | |||
| Balance | < 0.10 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | < 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C, Injection Molded) | 22.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation | |||
| Yield, 23°C, injection molding | 100 | % | ASTM D638 |
| Fracture, 23°C, injection molding | 100 | % | ISO 527-2 |
| Flexural Modulus (23°C, Injection Molded) | 1100 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C, injection molding | 360 | J/m | ASTM D256 |
| 23°C, injection molding | 40 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 97.0 | °C | ISO 306/A50, ASTM D1525 1 |
| Heat Distortion | |||
| -- | 75 | °C | ISO 75-2 |
| -- | 75 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | ASTM D257 |
| Dielectric Strength (23°C) | 160 | kV/mm | ASTM D149 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 160 - 180 | °C | |
| Middle Temperature | 180 - 200 | °C | |
| Front Temperature | 190 - 210 | °C | |
| Nozzle Temperature | 210 - 230 | °C |
| Injection instructions |
|---|
| Zone 4: 200 - 220°C |
| Note Message | |
|---|---|
| 1 . | 速率 A (50°C/h), 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® N8960T | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| TAISOX 9000 | Formosa Plastics Corporation | HDPE | TAISOX |
| ELASTOSIL® M 4440 | Wacker Chemie AG | Silicone | ELASTOSIL® M |
| Lifoflex® UVX 63.01 B045 | ELASTO | TPE | Lifoflex® |
| Karina WHITE PVC COMPOUND 752D10/151-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |