UNITHENE® LH901
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | USI Corporation |
| Trademark: | UNITHENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1w7vpY_UNITHENE-LH901.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
UNITHENE LH901 is a high density polyethylene (HDPE) especially used for the extrusion of filament and sheet. A combination of excellent stretchability, less melt fracture, high tenacity and good processability makes it be suitably tailored for the fabrication of fishing nets, ropes, windows screen, upholstery, filters, woven sacks, canvas laminated cloth and various other industrial and ornamental knitted items. In addition, it can be applied to the manufacture of sheet, thin film and molded articles with good resistance to stress cracking. UNITHENE LH901 can be easily pigmented to any color by either dry blending or melt blending of the masterbatch into the resin. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.953 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | 0.95 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 68 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 1% Secant (Compression Molded) | 726 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 24.5 | MPa | ASTM D638 |
| Fracture | 29.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1100 | % | ASTM D638 |
| Apparent Bending Modulus | 1080 | MPa | ASTM D747 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 540 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 125 | °C | ASTM D1525 |
| Peak Melting Temperature | 131 | °C | ASTM D3418 |
| Additional Information |
|---|
| Torsional Stiffness, ASTM D1043: 6100 kg/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3782 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| UBE Nylon 1015GC6 | UBE Engineering Plastics, S.A. | Nylon 6 | UBE Nylon |
| Fainplast PVC PHS 60 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Perfactory® HTM140IV | EnvisionTEC, Inc. | Acrylic, Unspecified | Perfactory® |
| ALCOM® MED PS 1000 AS 14114 | ALBIS PLASTIC GmbH | PS (HIPS) | ALCOM® MED PS |