KumhoSunny PA/ABS HNB0225G2
| Category: | ABS+Nylon , Acrylonitrile Butadiene Styrene + Nylon |
| Manufacturer: | Shanghai KumhoSunny Plastics Co., Ltd. |
| Trademark: | KumhoSunny PA/ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1w0SfO_KumhoSunny-PA-ABS-HNB0225G2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HNB 0225G2 has the feature that 10%GF is contained. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.14 | g/cm³ | ASTM D792 |
| -- | 1.13 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 240°C/10.0 kg | 15 to 25 | g/10 min | ASTM D1238 |
| 240°C/10.0 kg | 20 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.30 to 0.80 | % | ASTM D955 |
| -- | 0.30 to 0.60 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 60.0 | MPa | ASTM D638 |
| -- | 53.0 | MPa | ISO 527-2/50 |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638 |
| Flexural Modulus | |||
| -- | 3000 | MPa | ASTM D790 |
| -- 1 | 2800 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 90.0 | MPa | ASTM D790 |
| -- 2 | 85.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3 | ISO 179 | ||
| -30°C | 10 | kJ/m² | |
| 23°C | 17 | kJ/m² | |
| Notched Izod Impact | |||
| 3.20 mm | 160 | J/m | ASTM D256 |
| 23°C 4 | 14 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 160 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 100 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 5 | 95.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 110 | °C | ASTM D1525 6 |
| -- | 115 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+14 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.020 | % | |
| Rear Temperature | 190 to 210 | °C | |
| Middle Temperature | 210 to 230 | °C | |
| Front Temperature | 210 to 230 | °C | |
| Nozzle Temperature | 220 to 240 | °C | |
| Processing (Melt) Temp | 220 to 230 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C | |
| Back Pressure | 1.00 to 5.00 | MPa | |
| Screw Speed | 30 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 4J |
| 4 . | 5.5J |
| 5 . | 120°C/h |
| 6 . | Rate B (120°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Chemlon® MDS4 | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| ColorFast® NY2GF130 | LTL Color Compounders, Inc. | Nylon 66 | ColorFast® |
| KEBATRON® PPS C2040G5 | BARLOG plastics GmbH | PPS | KEBATRON® |
| Lumiloy® GN2101F | LG Chem Ltd. | PPE+PS | Lumiloy® |
| LEXAN™ XHT1171 resin | SABIC Innovative Plastics | PC | LEXAN™ |