Tarnoform® 300 GF6 TF3
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Grupa Azoty S.A. |
| Trademark: | Tarnoform® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1vKi3P_Tarnoform-300-GF6-TF3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Tarnoform® 300 GF6 TF3 there is 30% glass fibres reinforced injection-moulding grade modified with PTFE increased tribological characteristics of this grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.72 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.0 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 1.50 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 180 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10000 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 105 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.5 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 9000 | MPa | ISO 178 |
| Flexural Stress 2 | 160 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 35 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | 6.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 150 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 145 | °C | ISO 306/B |
| Melting Temperature | 167 | °C | ISO 11357-3 |
| Limit of Temperature - a few hours operation | 100 | °C |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | FMVSS 302 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Type | POM-K, M-GNRS, 01-003, GF30 | ISO 1874 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.10 | % | |
| Suggested Max Regrind | 10 | % | |
| Processing (Melt) Temp | 180 to 230 | °C | |
| Mold Temperature | 80.0 to 110 | °C | |
| Injection Pressure | 80.0 to 110 | MPa | |
| Injection Rate | Slow-Moderate |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| BITONER® TR-120 | Qingdao Bater Chemical Co., Ltd. | TP, Unspecified | BITONER® |
| ASI POLYPROPYLENE 828-01 | A. Schulman Inc. | PP Impact Copolymer | ASI POLYPROPYLENE |
| DJSilicone NE-G161 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| Pemex BDL 92020 S | Pemex Petroquímica | LLDPE | Pemex |
| Sylvin 8240-80 White 1584 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |