LNP™ VERTON™ RV00AE compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ VERTON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1vK3Oz_LNP-VERTON-RV00AE-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP VERTON RV00AE is a compound based on Nylon 66 containing 50% Long Glass Fiber. Added features of this grade include: Easy Molding, Structural. Also known as: LNP* VERTON* Compound RF-700-10-EM Product reorder name: RV00AE |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.59 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.10 to 0.30 | % | |
| Across Flow : 24 hr | 0.40 to 0.60 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.64 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.2 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 15700 | MPa | ASTM D638 |
| -- | 14500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 219 | MPa | ASTM D638 |
| Break | 216 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 2.1 | % | ASTM D638 |
| Break | 2.3 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 13200 | MPa | ASTM D790 |
| -- 5 | 13300 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 342 | MPa | ISO 178 |
| Yield, 50.0 mm Span 6 | 362 | MPa | ASTM D790 |
| Break, 50.0 mm Span 7 | 359 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 390 | J/m | ASTM D256 |
| 23°C 8 | 42 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1300 | J/m | ASTM D4812 |
| 23°C 9 | 83 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 15.5 | J | ASTM D3763 |
| -- | 8.30 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 226 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 224 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 223 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 222 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 282 to 293 | °C | |
| Middle Temperature | 288 to 299 | °C | |
| Front Temperature | 288 to 299 | °C | |
| Processing (Melt) Temp | 288 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUNVIEO™ A7171 | Asahi Kasei Chemicals Corporation | TPV | SUNVIEO™ |
| Monprene® CP-13022D | Teknor Apex Company | TPE | Monprene® |
| Zhongfa PP FR-08 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PP, Unspecified | Zhongfa |
| NuSil MED-1131 | NuSil Technology | Silicone | NuSil |
| CP PRYME® Polypropylene PPH100-.7FM | Chase Plastics Services Inc. | PP Homopolymer | CP PRYME® Polypropylene |