Borealis PE FT6230
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Borealis AG |
| Trademark: | Borealis PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1uYc6L_Borealis-PE-FT6230.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FT6230 is a tubular, low density, polyethylene grade for the production of packaging film. FT6230 is developed to give films with good optical properties for thin film applications. FT6230 is intended for applications like:
FT6230 contains no additives. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic) | 0.60 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| MD : 40 µm | 180 | MPa | ASTM D882 |
| TD : 40 µm | 190 | MPa | ASTM D882 |
| Tensile Strength | ISO 527-3 | ||
| MD : 40 µm | 25.0 | MPa | ISO 527-3 |
| TD : 40 µm | 20.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 40 µm | 300 | % | ISO 527-3 |
| TD : Break, 40 µm | 600 | % | ISO 527-3 |
| Dart Drop Impact (40 µm) | 100 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 40 µm | 3.0 | N | ISO 6383-2 |
| TD : 40 µm | 2.0 | N | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 95.0 | °C | ISO 306/A50 |
| Melting Temperature (DSC) | 111 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (1020 µm) | 90 | ASTM D2457 | |
| Haze (1020 µm) | 8.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 - 180 | °C |
| Extrusion instructions |
|---|
| Blow Up Ratio: 1:2.5 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Melinex® 052 | DuPont Teijin Films U.S. | Polyester, TP | Melinex® |
| Modified Plastics MN 6/6-FG 40 | Modified Plastics, Inc. | Nylon 66 | Modified Plastics |
| Visiloy™ 2653U2 | Technical Polymers, LLC | PC+PBT | Visiloy™ |
| Andur 9-APF-LM/Curene3005/St105 | Anderson Development Company | PUR-Ester/TDI | Andur |
| HiFill FR® PC IM FR | Techmer Engineered Solutions | PC | HiFill FR® |