TIPELIN® 6000B
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | MOL Petrochemicals Co. Ltd. |
| Trademark: | TIPELIN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1tt2MY_TIPELIN-6000B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TIPELIN 6000B is a high density bimodal polyethylene copolymer (with butene-1 as comonomer) intended for blow moulding of products with high stiffness and very good environmental stress crack resistance (ESCR) The grade contains antioxidant and acid scavenger. Applications TIPELIN 6000B is recommended for thin walled, small bottles up to 5 litre capacity for consumer goods such as cosmetics, daily care etc. and for blow moulded products for packaging of aggressive industrial chemicals bounded to UN certificates. It is suitable for corrugated pipes too. TIPELIN 6000B is suitable for food contact, for manufacturing of pharmaceutical packing products and toys. The product complies with Food Contact, Pharmaceutical and Toy Safety Regulations. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.958 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.30 | g/10 min | |
| 190°C/21.6 kg | 30 | g/10 min | |
| 190°C/5.0 kg | 1.3 | g/10 min | |
| Environmental Stress-Cracking Resistance (10% Igepal CO-630, F50) | 200 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 65 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 32.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 11 | % | |
| Break | 1400 | % | |
| Flexural Modulus | 1700 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 9.0 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 127 | °C | ISO 306/A120 |
| Oxidation Induction Time (200°C) | 30 | min | EN 728 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 to 165 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tisoplen® PPH 40 MNF TALC | Tisan | PP Homopolymer | Tisoplen® |
| WONDERLITE® PC-110V | CHI MEI CORPORATION | PC | WONDERLITE® |
| Capilene® SW 75 AV | Carmel Olefins Ltd. | PP Impact Copolymer | Capilene® |
| Emulprene® 1028A | INSA | SBR, Emulsion | Emulprene® |
| LNP™ THERMOCOMP™ DF0049 compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |