NOVADURAN® 5010N6-3X
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | NOVADURAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1tE62C_NOVADURAN-5010N6-3X.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NOVADURAN® 5010N6-3X is a Polybutylene Terephthalate (PBT) material. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of NOVADURAN® 5010N6-3X are:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.43 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Across Flow : 2.00 mm | 1.8 | % | |
| Flow : 2.00 mm | 1.9 | % | |
| Water Absorption (Saturation, 23°C) | 0.080 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2800 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 57.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 4.0 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 20 | % | ISO 527-2 |
| Flexural Modulus | 2500 | MPa | ISO 178 |
| Flexural Stress | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 120 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 165 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 77.0 | °C | ISO 75-2/A |
| Melting Temperature | 224 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow : -30 to 50°C | 8.0E-5 | cm/cm/°C | |
| Flow : -30 to 120°C | 1.2E-4 | cm/cm/°C | |
| Flow : 50 to 120°C | 1.5E-4 | cm/cm/°C | |
| Transverse : -30 to 50°C | 9.0E-5 | cm/cm/°C | |
| Transverse : -30 to 120°C | 1.2E-4 | cm/cm/°C | |
| Transverse : 50 to 120°C | 1.5E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength | IEC 60243-1 | ||
| 1.00 mm | 21 | kV/mm | |
| 2.00 mm | 18 | kV/mm | |
| Relative Permittivity (1 MHz) | 3.20 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.020 | IEC 60250 | |
| Comparative Tracking Index (CTI) | PLC 1 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.710 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 5.0 to 8.0 | hr | |
| Rear Temperature | 235 | °C | |
| Middle Temperature | 240 | °C | |
| Front Temperature | 250 | °C | |
| Nozzle Temperature | 245 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Pressure | 20.0 to 150 | MPa | |
| Screw Speed | 80 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Relpet® G5761 | Reliance Industries Limited | PET | Relpet® |
| Shandong PA612 Type II | Shandong Guangyin New Materials Co., Ltd. | Nylon 612 | Shandong PA612 |
| TEPCON® M90 | Polyplastics Co., Ltd. | Acetal (POM) Copolymer | TEPCON® |