Quadrant EPP Nylatron® LFG Nylon
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Quadrant Engineering Plastic Products |
| Trademark: | Quadrant EPP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1sWEbN_Quadrant-EPP-Nylatron-LFG-Nylon.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Quadrant EPP Nylatron® LFG Nylon is a Polyamide 6 (Nylon 6) product. It can be processed by casting and is available in North America. Typical application: Food Contact Applications. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.30 | % | |
| Saturation | 6.0 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 85 | ||
| R-Scale | 120 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3210 | MPa | ASTM D638 |
| Tensile Strength (Ultimate) | 68.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 50 | % | ASTM D638 |
| Flexural Modulus | 3620 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 103 | MPa | ASTM D790 |
| Compressive Modulus | 2280 | MPa | ASTM D695 |
| Compressive Strength (10% Strain) | 93.1 | MPa | ASTM D695 |
| Shear Strength | 64.1 | MPa | ASTM D732 |
| Coefficient of Friction (vs. Steel - Static) | 0.14 | Internal Method | |
| Wear Factor | 180 | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 80 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 93.3 | °C | ASTM D648 |
| Maximum Use Temperature - Long Term, Air | 104 | °C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Limiting Pressure Velocity 1 | 0.210 | MPa·m/s | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Crystallization Temperature (DSC) | 216 | °C | ASTM D3418 |
| CLTE - Flow 2(-40 to 149°C) | 1.0E-4 | cm/cm/°C | ASTM E831 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.18 mm, Estimated Rating) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 4:1 safety factor |
| 2 . | 68°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stylac™ IC39A | Asahi Kasei Chemicals Corporation | ABS | Stylac™ |
| Tygon F-4040-A | Saint Gobain - Norton | PVC, Unspecified | Tygon |
| BCC Resins BC 6005 | BCC Products Inc. | Epoxy | BCC Resins |
| Globalprene® 3522 | Lee Chang Yung Chemical Industry Corp. | SBS | Globalprene® |
| Hanwha Total TPE SE80 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | TPE | Hanwha Total TPE |