Lanufene LLF 182H
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Ras Lanuf Oil & Gas Processing Company (RASCO) |
| Trademark: | Lanufene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1rggQG_Lanufene-LLF-182H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LANUFENE LLF 182H is a linear low density polyethylene for general purpose blown film extrusion with high mechanical properties and good process-ability. LANUFENE LLF 182H contains slip additive and anti-blocking agent. The film produced from this resin characteristically exhibits good toughness, high tensile properties, outstanding puncture resistance and good optical properties. LANUFENE LLF 182H is recommended for the manufacture of thin gauged general purpose blown films such as industrial liners, food packaging and agricultural mulching film. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 2.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Ultimate) | 18.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 650 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 38 µm | 220 | MPa | |
| 1% Secant, TD : 38 µm | 260 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 38 µm | 34.0 | MPa | |
| TD : Break, 38 µm | 25.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 38 µm | 700 | % | |
| TD : Break, 38 µm | 750 | % | |
| Dart Drop Impact (38 µm) | 60 | g | ASTM D1709A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 95.0 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 38.0 µm) | 60 | ASTM D2457 | |
| Haze (38.0 µm) | 10 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 to 210 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecomid® NB40 GR20 NL XA60 | Eurotec Engineering Plastics | Nylon 6 | Tecomid® |
| Eltex® TUB121N3000 | INEOS Olefins & Polymers Europe | HDPE Copolymer | Eltex® |
| HIPOLEN P® EH 9 | HIPOL A.D. | PP Homopolymer | HIPOLEN P® |
| POLYCOMPO PE 5000S | POLYCOMPO Co.,Ltd. | HDPE | POLYCOMPO PE |
| Sylvin 2920-60 Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |