Lupoy® GN1006FM
| Category: | PC , Polycarbonate |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupoy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1r56Wx_Lupoy-GN1006FM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description Halogen Free Flame Retardant, Transparency Application IT/OA, Electric & Electronic Housing and Components |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 61.8 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 100 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2260 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 3.20 mm) | 91.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 720 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 130 | °C | ASTM D648 |
| Vicat Softening Temperature | 141 | °C | ASTM D1525 5 |
| RTI Elec | 120 | °C | UL 746 |
| RTI Imp | 110 | °C | UL 746 |
| RTI Str | 120 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-2 | ||
| 2.00 mm | V-1 | ||
| 2.50 mm | V-0 | ||
| 3.00 mm | V-0 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transparency | 87 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 260 to 280 | °C | |
| Middle Temperature | 280 to 300 | °C | |
| Front Temperature | 300 to 320 | °C | |
| Nozzle Temperature | 300 to 320 | °C | |
| Processing (Melt) Temp | 300 to 320 | °C | |
| Mold Temperature | 80.0 to 120 | °C | |
| Back Pressure | 0.981 to 3.92 | MPa | |
| Screw Speed | 40 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| 5 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Milastomer™ 9070NS | Mitsui Chemicals America, Inc. | TPV | Milastomer™ |
| SCHULABLEND® (ABS/PA) M/MK 8 GF | A. Schulman Europe | ABS+Nylon | SCHULABLEND® |
| Silopren® LSR 3485/50 | Momentive Performance Materials Inc. | Silicone Rubber, LSR | Silopren® |
| HyTemp® AR22 | Zeon Chemicals L.P. | Acrylic, Unspecified | HyTemp® |
| Sylvin 6034-85 Red 6268 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |