SCHULAMID® 6 MV 14 FR 4 K1681
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1pWfTG_SCHULAMID-6-MV-14-FR-4-K1681.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Medium viscosity flame-retardant Polyamide 6 grade (V-2); without PBDE |
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.26 | -- | g/cm³ | ISO 1183/A |
| Viscosity Number | 145 | -- | cm³/g | ISO 307 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 160 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3800 | 1250 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 70.0 | 35.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 3.0 | 24 | % | ISO 527-2/1A/50 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 3.0 | -- | kJ/m² | |
| 23°C | 4.0 | 18 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 48 | -- | kJ/m² | |
| 23°C | 49 kJ/m² | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 186 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 76.0 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | ||||
| -- | 217 | -- | °C | ISO 306/A50 |
| -- | 202 | -- | °C | ISO 306/B50 |
| Ball Pressure Test (200°C) | Pass | -- | IEC 60695-10-2 | |
| RTI Elec | UL 746 | |||
| 0.380 mm | 130 | -- | °C | |
| 0.750 mm | 130 | -- | °C | |
| 1.50 mm | 130 | -- | °C | |
| 3.00 mm | 130 | -- | °C | |
| RTI Imp | UL 746 | |||
| 0.380 mm | 75.0 | -- | °C | |
| 0.750 mm | 90.0 | -- | °C | |
| 1.50 mm | 100 | -- | °C | |
| 3.00 mm | 100 | -- | °C | |
| RTI Str | UL 746 | |||
| 0.380 mm | 100 | -- | °C | |
| 0.750 mm | 110 | -- | °C | |
| 1.50 mm | 120 | -- | °C | |
| 3.00 mm | 120 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index | 300 | -- | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | UL 746 | |||
| 0.380 mm | PLC 0 | -- | ||
| 0.750 mm | PLC 0 | -- | ||
| 1.50 mm | PLC 0 | -- | ||
| 3.00 mm | PLC 0 | -- | ||
| Hot-wire Ignition (HWI) | UL 746 | |||
| 0.380 mm | PLC 4 | -- | ||
| 0.750 mm | PLC 4 | -- | ||
| 1.50 mm | PLC 2 | -- | ||
| 3.00 mm | PLC 0 | -- |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | ISO 3795 | |||
| 0.380 mm, Self-Extinguishing | 0.0 | -- | mm/min | |
| 0.750 mm, Self-Extinguishing | 0.0 | -- | mm/min | |
| 1.50 mm, Self-Extinguishing | 0.0 | -- | mm/min | |
| 3.00 mm, Self-Extinguishing | 0.0 | -- | mm/min | |
| Flame Rating | UL 94, IEC 60695-11-10, -20 | |||
| 0.380 mm | V-2 | -- | ||
| 0.750 mm | V-2 | -- | ||
| 1.50 mm | V-2 | -- | ||
| 3.00 mm | V-2 | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.380 mm | 850 | -- | °C | |
| 0.750 mm | 850 | -- | °C | |
| 1.50 mm | 960 | -- | °C | |
| 3.00 mm | 960 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.380 mm | 825 | -- | °C | |
| 0.750 mm | 825 | -- | °C | |
| 1.50 mm | 825 | -- | °C | |
| 3.00 mm | 825 | -- | °C | |
| Oxygen Index | 23 | -- | % | ISO 4589-2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 175X | RTP Company | PP, Unspecified | RTP |
| Sindustris PC GN5102RF | Sincerity Australia Pty Ltd. | PC | Sindustris PC |
| BP RPPC 1020 TU BLK | Buckeye Polymers, Inc. | PP Copolymer | BP |
| LNP™ THERMOCOMP™ UC006XXH compound | SABIC Innovative Plastics | PPA | LNP™ THERMOCOMP™ |
| PLUSTEK PA804 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |