LNP™ THERMOTUF™ QX01581H compound
| Category: | Nylon 610 , Polyamide 610 |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ THERMOTUF™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1o0HIm_LNP-THERMOTUF-QX01581H-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOTUF QX01581H is a compound based on Nylon 6/10 resin containing Glass Fiber. Added features of this material include: High Impact. Also known as: LNP* THERMOTUF* Compound PDX-Q-01581 Product reorder name: QX01581H |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.10 to 0.30 | % | ASTM D955, ISO 294-4 |
| Across Flow : 24 hr | 0.90 to 1.1 | % | ASTM D955 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.20 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 8480 | MPa | ASTM D638 |
| -- | 7880 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 140 | MPa | ASTM D638 |
| Break | 134 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 3.4 | % | ASTM D638 |
| Break | 3.6 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 7030 | MPa | ASTM D790 |
| -- | 7250 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 207 | MPa | ASTM D790 |
| -- | 208 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 360 | J/m | ASTM D256 |
| 23°C 2 | 15 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1200 | J/m | ASTM D4812 |
| 23°C 3 | 73 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 9.30 | J | ASTM D3763 |
| -- | 3.52 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 208 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 205 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 3.1E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 3.2E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 8.8E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP PHC31-81 | Saudi Basic Industries Corporation (SABIC) | PP Impact Copolymer | SABIC® PP |
| Starex BC-0140 H | SAMSUNG SDI CO., LTD. | ABS | Starex |
| New-prene™ 6185N | Total Polymer Vision (Suzhou) Co., LTD | PP+EPDM | New-prene™ |
| ENSOFT SU-141-20A | ENPLAST, a Ravago Group Company | TPE | ENSOFT |
| LEXAN™ HPH4504H resin | SABIC Innovative Plastics | PPC | LEXAN™ |