Sup-tech T9000
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Shanghai Suptech Engineering Plastics Co. Ltd. |
| Trademark: | Sup-tech |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1lCeRk_Sup-tech-T9000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sup-tech T9000 is a Polybutylene Terephthalate (PBT) product. It can be processed by injection molding and is available in Asia Pacific. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.25 | g/cm³ | DIN 53479 |
| Molding Shrinkage | 0.011 to 0.015 | % | DIN 53464 |
| Water Absorption | DIN 53495 | ||
| 23°C, 24 hr | 0.050 | % | |
| Saturation, 23°C | 0.060 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 55.0 | MPa | DIN 53455 |
| Tensile Strain (Break) | 5.0 | % | DIN 53452 |
| Flexural Modulus | 2200 | MPa | DIN 53457 |
| Flexural Stress | 80.0 | MPa | DIN 53457 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.0 | kJ/m² | DIN 53453 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | DIN 53461 | ||
| 0.45 MPa, Unannealed | 170 | °C | |
| 1.8 MPa, Unannealed | 60.0 | °C | |
| Melting Temperature | 220 to 225 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Electric Strength | 20 | kV/mm | DIN 53481 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 4.0 to 10 | hr | |
| Processing (Melt) Temp | 230 to 255 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrant EPP Proteus® White | Quadrant Engineering Plastic Products | PP Homopolymer | Quadrant EPP |
| VAMPLUB F 00U 44TFGr | Vamp Tech | PPS | VAMPLUB |
| Hostaform® WR140LG | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| ISOTHANE® 3095A | Great Eastern Resins Industrial Co Ltd (GRECO) | TPU-Polyether | ISOTHANE® |
| Mitsui EPT™ 9090M | Mitsui Chemicals, Inc. | EPDM | Mitsui EPT™ |