This product is a polyurethane system.
If required special formulations for density between 0,1 g/cm³ and 0,5 g/cm³ possible.

Applications

Styling models

Laminate molds

Base constructions

Negatives

Properties

density 200 g/l

good milling

very good surface structure

easy to machine

very good flowability

good heat resistance

General Information
Features	Foamable Good Flow Machinable Medium Heat Resistance
Uses	Foam Molds/Dies/Tools
Appearance	Beige
Processing Method	Casting

Physical	Nominal Value	Unit	Test Method
Density ¹	0.180 to 0.220	g/cm³

Hardness	Nominal Value	Unit	Test Method
Shore Hardness			ISO 7619
Shore A	70 to 75
Shore D	18 to 22

Mechanical	Nominal Value	Unit	Test Method
Compressive Stress	2.30 to 2.50	MPa	ISO 604

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (0.45 MPa, Unannealed)	51.0 to 53.0	°C	ISO 75-2/B
CLTE - Flow	7.7E-5	cm/cm/°C	DIN 53752

Thermoset	Nominal Value	Unit
Thermoset Components
Hardener	Mix Ratio by Weight: 80
Resin	Mix Ratio by Weight: 100

Uncured Properties	Nominal Value	Unit
Density (20°C)	1.20	g/cm³

Note Message
1 .	Cured

Resin Grade	Manufacturer	Category	Trademark
Hostaform® C 27021 AS	Celanese Corporation	Acetal (POM) Copolymer	Hostaform®
LEXAN™ PC0700 resin	SABIC Innovative Plastics Asia Pacific	PC	LEXAN™
LNP™ LUBRICOMP™ LCL33E compound	SABIC Innovative Plastics	PEEK	LNP™ LUBRICOMP™
LNP™ THERMOCOMP™ D251 compound	SABIC Innovative Plastics Asia Pacific	PC	LNP™ THERMOCOMP™
3M™ Dyneon™ PTFE Compound TF R6703	3M Advanced Materials Division	PTFE	3M™ Dyneon™ PTFE Compound