VENYL UG308
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AD majoris |
| Trademark: | VENYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1kqxEY_VENYL-UG308.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VENYL UG308 is a 35% glass fibre reinforced polyamide 66 for Injection moulding. APPLICATIONS VENYL UG308 has been developed especially for very demanding applications in automotive industry and electrical parts requiring excellent combination between thermal and mechanical properties. VENYL UG308 is available in black (VENYL UG308-8229) and other colours can be provided on request. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.39 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.50 to 0.70 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.5 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (L-Scale) | 110 | 108 | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 10000 | 7000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 200 | 140 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | 3.0 | % | ISO 527-2 |
| Flexural Modulus | 9500 | 7000 | MPa | ISO 178 |
| Flexural Stress | 280 | 245 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 10 | 14 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 40 | 50 | kJ/m² | ISO 179 |
| Notched Izod Impact | 100 | 150 | J/m | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 261 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 252 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 256 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+11 | ohms | DIN 53482 |
| Volume Resistivity | 1.0E+14 | 1.0E+12 | ohms·cm | DIN 53482 |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 750 | -- | °C | IEC 60695-2-12 |
| Oxygen Index | 24 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 285 to 300 | °C | |
| Middle Temperature | 280 to 295 | °C | |
| Front Temperature | 275 to 290 | °C | |
| Nozzle Temperature | 265 to 280 | °C | |
| Mold Temperature | 90.0 to 120 | °C | |
| Injection Pressure | 85.0 to 110 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 to 70.0 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4000 AT-1001 L | RTP Company | PPA | RTP |
| SLOVALEN® PH 49 GF 40 | Plastcom | PP, Unspecified | SLOVALEN® |
| Sumitomo PP AR764 | Sumitomo Chemical Asia | PP Copolymer | Sumitomo PP |
| Wah Hong DAP WH-9100- BLK D | Wah Hong Industrial Corp. | DAP | Wah Hong DAP |
| Yuyao PP PP Glass-filled | Yuyao Tenglong Plastics Co., Ltd. | PP, Unspecified | Yuyao PP |