Lucky Enpla LAY1004EX
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Lucky Enpla Co LTD |
| Trademark: | Lucky Enpla |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1k5gGH_Lucky-Enpla-LAY1004EX.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lucky Enpla LAY1004EX is a polycarbonate acrylonitrile butadiene styrene (PC ABS) product,. It can be processed by extrusion or injection molding and is available in North America, Europe or Asia Pacific. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 - 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 61.8 | MPa | ASTM D638 |
| Flexural Modulus 2 | 2260 | MPa | ASTM D790 |
| Flexural Strength 3 | 89.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (3.18 mm) | 690 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 120 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 90.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Rear Temperature | 230 - 250 | °C | |
| Middle Temperature | 235 - 255 | °C | |
| Front Temperature | 250 - 270 | °C | |
| Nozzle Temperature | 250 - 270 | °C | |
| Mold Temperature | 30.0 - 60.0 | °C | |
| Back Pressure | 0.490 - 1.47 | MPa | |
| Screw Speed | 40 - 70 | rpm |
| Injection instructions |
|---|
| Resin Temperature: 250-270°CInjection Pressure (1st Pressure): 800-1200 kg/cm²Injection Pressure (2nd Pressure): 300-700 kg/cm² |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 10 mm/min |
| 3 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SAXALEN™ PPH304G25 | SAX Polymers | PP Homopolymer | SAXALEN™ |
| Crastin® PC164 NC010 | DuPont Performance Polymers | PBT | Crastin® |
| Kingfa MAC-751 | Kingfa | PC+ABS | Kingfa |
| MAJORIS DEG388 - 8651 | AD majoris | PP, Unspecified | MAJORIS |
| MARPOL® EVA 602 | Marco Polo International, Inc. | EVA | MARPOL® EVA |