XENOY™ 6370 resin
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | XENOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1ibr0C_XENOY-6370-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% glass-reinforced, impact modified thermoplastic alloy. Improved toughness and ductility. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.44 | g/cm³ | ASTM D792, ISO 1183 |
| Specific Volume | 0.700 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/5.0 kg) | 24 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 250°C/5.0 kg | 12.0 | cm³/10min | |
| 265°C/5.0 kg | 19.0 | cm³/10min | |
| Molding Shrinkage | Internal Method | ||
| Flow 1 | 0.30 to 0.40 | % | |
| Flow 2 | 0.40 to 0.50 | % | |
| Across Flow 3 | 0.40 to 0.70 | % | |
| Across Flow 4 | 0.70 to 0.90 | % | |
| Water Absorption | |||
| 24 hr | 0.090 | % | ASTM D570 |
| Saturation, 23°C | 0.50 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.15 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 109 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 5 | 9750 | MPa | ASTM D638 |
| -- | 8500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 6 | 97.0 | MPa | ASTM D638 |
| Yield | 105 | MPa | ISO 527-2/5 |
| Break 7 | 91.0 | MPa | ASTM D638 |
| Break | 3.00 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 8 | 3.0 | % | ASTM D638 |
| Yield | 3.0 | % | ISO 527-2/5 |
| Break 9 | 4.0 | % | ASTM D638 |
| Break | 110 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 10 | 5380 | MPa | ASTM D790 |
| -- 11 | 7750 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 154 | MPa | ISO 178 |
| Yield, 50.0 mm Span 12 | 150 | MPa | ASTM D790 |
| Break, 50.0 mm Span 13 | 138 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 14(23°C) | 9.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 110 | J/m | ASTM D256 |
| 23°C | 170 | J/m | ASTM D256 |
| -30°C 15 | 6.0 | kJ/m² | ISO 180/1A |
| 23°C 16 | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | 640 | J/m | ASTM D4812 |
| Instrumented Dart Impact | ASTM D3763 | ||
| 23°C, Energy at Peak Load | 5.00 | J | |
| 23°C, Total Energy | 17.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 204 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 163 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 6.40 mm | 149 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 17 | 155 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 153 | °C | ASTM D1525 18 |
| -- | 148 | °C | ISO 306/B50 |
| -- | 150 | °C | ISO 306/B120 |
| CLTE | |||
| Flow : -40 to 40°C | 2.7E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Flow : 60 to 138°C | 2.0E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 1.1E-4 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| RTI Elec | 140 | °C | UL 746 |
| RTI Imp | 130 | °C | UL 746 |
| RTI Str | 140 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 4.8E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | ASTM D149 | ||
| 1.60 mm, in Oil | 27 | kV/mm | |
| 3.20 mm, in Air | 20 | kV/mm | |
| Dielectric Constant | ASTM D150 | ||
| 100 Hz | 4.00 | ||
| 1 MHz | 4.00 | ||
| Dissipation Factor | ASTM D150 | ||
| 100 Hz | 3.0E-3 | ||
| 1 MHz | 0.020 | ||
| Arc Resistance 19 | PLC 5 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 3 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 1 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 1 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 50 to 80 | % | |
| Rear Temperature | 249 to 271 | °C | |
| Middle Temperature | 254 to 277 | °C | |
| Front Temperature | 260 to 282 | °C | |
| Nozzle Temperature | 254 to 277 | °C | |
| Processing (Melt) Temp | 260 to 282 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C | |
| Back Pressure | 0.345 to 0.552 | MPa | |
| Screw Speed | 50 to 80 | rpm | |
| Vent Depth | 0.013 to 0.020 | mm |
| Note Message | |
|---|---|
| 1 . | 0.75 to 2.3 mm |
| 2 . | 2.3 to 4.6 mm |
| 3 . | 0.75 to 2.3 mm |
| 4 . | 2.3 to 4.6 mm |
| 5 . | 5.0 mm/min |
| 6 . | Type I, 5.0 mm/min |
| 7 . | Type I, 5.0 mm/min |
| 8 . | Type I, 5.0 mm/min |
| 9 . | Type I, 5.0 mm/min |
| 10 . | 1.3 mm/min |
| 11 . | 2.0 mm/min |
| 12 . | 1.3 mm/min |
| 13 . | 1.3 mm/min |
| 14 . | 80*10*4 sp=62mm |
| 15 . | 80*10*4 |
| 16 . | 80*10*4 |
| 17 . | 80*10*4 mm |
| 18 . | Rate B (120°C/h), Loading 2 (50 N) |
| 19 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVALEN® PQ 53 N | Plastcom | PP, Unspecified | SLOVALEN® |
| SUPREME PP SPEXP64 | Supreme Petrochem Ltd. | PP, Unspecified | SUPREME PP |
| Cri-Line IF-715 | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |
| G-Lex B63A003 | Gas Authority of India Limited | HDPE | G-Lex |
| SQUARE® LIM1962-50A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |