OP - PPO PPOX-210
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Oxford Polymers |
| Trademark: | OP - PPO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1iBWmW_OP---PPO-PPOX-210.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| OP-PPO PPOX-210 is a polyphenylene ether PS (PPE PS) material,. This product is available in North America and is processed by injection molding. The main characteristics of OP-PPO PPOX-210 are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (315°C/5.0 kg) | 25 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 - 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 34.5 | MPa | ASTM D638 |
| Fracture | 34.5 | MPa | ASTM D638 |
| Flexural Modulus | 1760 | MPa | ASTM D790 |
| Flexural Strength | 48.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (4°C) | 270 | J/m | ASTM D256 |
| Dart Drop Impact | 14.1 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.18mm | 98.9 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.18mm | 93.3 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.59 mm | HB | UL 94 | |
| 3.18 mm | HB | UL 94 |
| Additional Information |
|---|
| Melt Mass -Flow Rate (MFR), ASTM D1238, 315°C/ 5.0kg: 20 to 30 g/10 min |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 - 110 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 249 - 293 | °C | |
| Middle Temperature | 260 - 304 | °C | |
| Front Temperature | 271 - 310 | °C | |
| Processing (Melt) Temp | 288 - 316 | °C | |
| Mold Temperature | 71.1 - 98.9 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ARMAMID® PA SVMN 30.1 | Poly Plastic | Nylon 6 | ARMAMID® |
| Chemlon® 115 G | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| Formolene® 6510A | Formosa Plastics Corporation, U.S.A. | PP Impact Copolymer | Formolene® |
| Hostacom TRC 352N | LyondellBasell Industries | Polyolefin, Unspecified | Hostacom |
| LNP™ VERTON™ MV00AS compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ VERTON™ |