POLYNIL® P50 FI
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Nilit Plastics |
| Trademark: | POLYNIL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1hiWgA_POLYNIL-P50-FI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
POLYNIL® P50 FI is an unreiforced Polyamide 66 (Nylon 66) for injection molding, UL listed V2. This general pourpose 2.7 viscosity Polyamide 66 resin is internally lubricated. POLYNIL® P50 FI is FDA compliant. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.14 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 23°C | 1.6 | % | |
| Flow : 23°C | 1.4 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 1.5 | % | |
| Saturation, 23°C | 8.5 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3100 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 83.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield, 23°C | 6.0 | % | |
| Break, 23°C | 50 | % | |
| Flexural Modulus (23°C) | 2900 | MPa | ISO 178 |
| Flexural Stress (23°C) | 120 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 4.5 | kJ/m² | |
| 23°C | 5.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| 23°C | No Break | ||
| 30°C | No Break | ||
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C | 4.5 | kJ/m² | |
| 23°C | 5.5 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 225 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 72.0 | °C | ISO 75-2/A |
| Continuous Use Temperature 1 | 85.0 | °C | IEC 60216 |
| Vicat Softening Temperature | 240 | °C | ISO 306/B |
| Ball Pressure Test | IEC 60695-10-2 | ||
| 125°C | Pass | ||
| 165°C | Pass | ||
| Melting Temperature | 258 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 2 | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength (2.00 mm) | 18 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (3.20 mm, Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-2 | ||
| 3.20 mm | V-2 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.800 mm | 750 | °C | |
| 3.20 mm | 850 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.800 mm | 775 | °C | |
| 3.20 mm | 750 | °C | |
| Oxygen Index | 28 | % | ISO 4589-2 |
| Flammability 3 | SE | FMVSS 302 |
| Note Message | |
|---|---|
| 1 . | 20000 hr |
| 2 . | 23°C |
| 3 . | 355x100x1mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Addisil™ 442 E | Momentive Performance Materials Inc. | Rubber | Addisil™ |
| Boda BDF401HP | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| FHR Polypropylene P4C5T-013 | Flint Hills Resources, LP | PP Homopolymer | FHR Polypropylene |
| Latiohm 82-01 CNT | LATI S.p.A. | Nylon 12 | Latiohm |
| SQUARE® LSR6060-30 | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |