Generic PUR-Ester/MDI
| Category: | PUR-Ester/MDI , Polyurethane (Polyester, MDI) |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1hDi0S_Generic-PUR-Ester-MDI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PUR-Ester/MDI This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 - 1.16 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (23°C) | 49 - 97 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compressive Strength (23°C) | 0.172 - 6.91 | MPa | ASTM D695 |
| Taber Abrasion Resistance (23°C) | 3.50 - 29.5 | mg | ASTM D1044 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Trouser Tear Resistance | 17.5 - 68.3 | N/mm | ISO 6383-1 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain, 23°C | 0.758 - 12.9 | MPa | ASTM D412 |
| 300% strain, 23°C | 1.21 - 25.2 | MPa | ASTM D412 |
| Tensile Strength | ASTM D412 | ||
| Yield, 23°C | 16.2 - 51.7 | MPa | ASTM D412 |
| Fracture, 23°C | 12.3 - 52.6 | MPa | ASTM D412 |
| 23°C | 18.7 - 53.8 | MPa | ASTM D412 |
| Tensile Elongation (Break, 23°C) | 340 - 750 | % | ASTM D412 |
| Tear Strength | |||
| 23°C | 15.8 - 139 | kN/m | ASTM D624 |
| Cracking | 20 | kN/m | ASTM D470 |
| Compression Set | 22 - 53 | % | ASTM D395 |
| Bayshore Resilience | 25 - 57 | % | ASTM D2632 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Pot Life (23°C) | 1.0 - 14 | min | |
| Thermoset Mix Viscosity | 350 - 859 | cP | ASTM D2393 |
| Demold Time | 1.0 - 1400 | min | |
| Post Cure Time | 16 - 20 | hr |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 100 - 125 | °C |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PUR-Ester/MDIThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A R 218 V33 BLACK 34 N | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| Trexprene® A80BW | Mitsubishi Chemical Performance Polymers, Inc. | TPV | Trexprene® |
| Hostacom TYC727D | LyondellBasell Industries | TPO (POE) | Hostacom |
| LNP™ THERMOCOMP™ RF008ESZ compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| PPO™ 630 resin | SABIC Innovative Plastics | PPE+PS | PPO™ |