EMERGE™ PC/PET 9100CR
| Category: | PC+PET , Advanced Resin |
| Manufacturer: | Trinseo |
| Trademark: | EMERGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1gvwG2_EMERGE-PC-PET-9100CR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EMERGE™ PC/PET 9100CR advanced resin is a polycarbonate blend with excellent chemical resistance. This grade was designed for use in medical equipment housings and can withstand repeated exposure to a variety of cleaners and disinfectants commonly used in hospitals. This grade has good aesthetics and excellent toughness. Main Characteristics:
Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 8.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.60 to 0.90 | % | |
| Across Flow | 0.50 to 0.80 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.20 mm, Injection Molded) | 111 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(3.20 mm, Injection Molded) | 2210 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield, 3.20 mm, Injection Molded | 50.0 | MPa | |
| Break, 3.20 mm, Injection Molded | 56.2 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield, 3.20 mm, Injection Molded | 4.7 | % | |
| Break, 3.20 mm, Injection Molded | 150 | % | |
| Flexural Modulus 4(3.20 mm, Injection Molded) | 2100 | MPa | ASTM D790 |
| Flexural Strength 5(3.20 mm, Injection Molded) | 77.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm, Injection Molded | 750 | J/m | |
| 23°C, 3.20 mm, Injection Molded | 910 | J/m | |
| Instrumented Dart Impact | ASTM D3763 | ||
| -40°C, 3.20 mm, Injection Molded, Peak Energy | 55.4 | J | |
| -40°C, 3.20 mm, Injection Molded, Total Energy | 80.2 | J | |
| 23°C, 3.20 mm, Injection Molded, Peak Energy | 46.3 | J | |
| 23°C, 3.20 mm, Injection Molded, Total Energy | 63.3 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 117 | °C | |
| 1.8 MPa, Unannealed | 87.2 | °C | |
| Vicat Softening Temperature | 144 | °C | ASTM D1525 6 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 4.3E+15 | ohms | IEC 60093 |
| Volume Resistivity | 3.4E+15 | ohms·cm | IEC 60093 |
| Electric Strength | IEC 60243-1 | ||
| 1.60 mm, in Oil | 28 | kV/mm | |
| 3.20 mm, in Oil | 17 | kV/mm | |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.28 | ||
| 1 MHz | 3.12 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 2.0E-3 | ||
| 1 MHz | 0.020 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 7(1.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 249 to 282 | °C | |
| Mold Temperature | 43.3 to 98.9 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | Rate B (120°C/h), Loading 1 (10 N) |
| 7 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® C 536XT NATURAL | Solvay Engineering Plastics | Nylon 6 | TECHNYL® C |
| Atlac 711-05AS | Reichhold Chemicals, Inc. | Polyester, TS | Atlac |
| Jianqiao Recycled PPGF30 | Shanghai Jianqiao Plastic Co., Ltd. | PP, Unspecified | Jianqiao |
| Lustran® 308 NR | INEOS Styrolution Group GmbH | ABS | Lustran® |
| LNP™ THERMOCOMP™ RFB66 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |