SABIC® PPcompound 8700
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1gsi8n_SABIC-PPcompound-8700.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PP elastomer modified MF for Injection moulding |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/5/50 | ||
| Yield, 3.20mm, injection molding | 20.0 | MPa | ISO 527-2/5/50 |
| Fracture, 3.20mm, injection molding | 16.0 | MPa | ISO 527-2/5/50 |
| Tensile Elongation 1(Break, 3.20 mm, Injection Molded) | 75 | % | ASTM D638 |
| Flexural Modulus 2(Injection Molded) | 1600 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | No Break | ISO 179/1eA | |
| Notched Izod Impact | ISO 180/4A | ||
| -20°C | 6.0 | kJ/m² | ISO 180/4A |
| 0°C | No Break | ISO 180/4A | |
| 23°C | No Break | ISO 180/4A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 95.0 | °C | ISO 75-2/B |
| CLTE - Flow | ASTM D696 | ||
| -30 to 30°C | 4.5E-5 | cm/cm/°C | ASTM D696 |
| 23 to 80°C | 9.9E-5 | cm/cm/°C | ASTM D696 |
| Additional Information |
|---|
| Mould shrinkage, SABIC method, 24 hours after injection moulding: 0.5% |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Method I (three-point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| QR Resin QR-5020 | QTR, Inc. | PEI+PC | QR Resin |
| Ming Dih EPS LSB | Ming Dih Group Corporation | PS (EPS) | Ming Dih EPS |
| HOPELEN H4540 | Lotte Chemical Corporation | PP Homopolymer | HOPELEN |
| Latene® EP 7 TES/30 | LATI S.p.A. | PP Copolymer | Latene® EP |
| INEOS PP T00G-00 | INEOS Olefins & Polymers USA | TPO | INEOS PP |