LNP™ STAT-KON™ EX02598C compound
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1gUUF7_LNP-STAT-KON-EX02598C-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON EX02598C is a compound based on Polyetherimide containing Proprietary Filler(s). Added features of this material include: Clean Compound System, Electrically Conductive. Also known as: LNP* STAT-KON* Compound PDX-E-02598 CCS Product reorder name: EX02598C |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.27 | g/cm³ | |
| -- | 1.26 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.60 to 0.80 | % | |
| Across Flow : 24 hr | 0.70 to 0.90 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3410 | MPa | ASTM D638 |
| -- | 3250 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 52.0 | MPa | ASTM D638 |
| Break | 60.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 1.7 | % | ASTM D638 |
| Break | 2.1 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 3310 | MPa | ASTM D790 |
| -- 5 | 3120 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 72.0 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 98.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 19 | J/m | ASTM D256 |
| 23°C 7 | 2.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 270 | J/m | ASTM D4812 |
| 23°C 8 | 18 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 2.80 | J | ASTM D3763 |
| -- | 0.920 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 172 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 171 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 163 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 160 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 5.0E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 5.4E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 3.0 to 6.0 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 343 to 354 | °C | |
| Middle Temperature | 354 to 366 | °C | |
| Front Temperature | 366 to 377 | °C | |
| Processing (Melt) Temp | 360 to 366 | °C | |
| Mold Temperature | 121 to 149 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ratron® 250G6 | Asia International Enterprise (Hong Kong) Limited | PESU | Ratron® |
| SEPAZ™ LC40 | Mando Advanced Materials Co., Ltd. | PP Copolymer | SEPAZ™ |
| Titalon® 4100GF | Titan Plastics Compounds Co., Ltd. | Nylon 46 | Titalon® |
| NuSil CF16-2186 | NuSil Technology | Silicone | NuSil |
| Sylvin 9048-85 Clear Brown 7304 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |