Hytrel® RS R4275 BK316
| Category: | TPC-ET , Thermoplastic Copolyester Elastomer |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Hytrel® RS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1g4iD9_Hytrel-RS-R4275-BK316.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 55 Shore D, Renewably Sourced, High Viscosity Polyester Elastomer with Good Heat Ageing Protection Developed for Blow Molding |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.17 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/10.0 kg) | 6.0 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/10.0 kg) | 6.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.9 | % | |
| Flow | 1.4 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 2.00 mm | 0.50 | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 0.20 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 50 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 150 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Break | 35.0 | MPa | |
| 5.0% Strain | 6.40 | MPa | |
| 10% Strain | 10.0 | MPa | |
| 50% Strain | 16.0 | MPa | |
| 100% Strain | 21.0 | MPa | |
| Tensile Strain (Break) | > 300 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 140 | MPa | |
| 1000 hr | 90.0 | MPa |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength - Flow | 140 | kN/m | ISO 34-1 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C | 45 | kJ/m² | |
| -30°C, Partial Break | 160 | kJ/m² | |
| 23°C | No Break | ||
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Tensile Impact Strength (23°C) | 500 | kJ/m² | ISO 8256/1 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -70.0 | °C | ISO 974 |
| Glass Transition Temperature 1 | -30.0 | °C | ISO 11357-2 |
| Melting Temperature 2 | 190 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 1.8E-4 | cm/cm/°C | |
| Transverse | 1.9E-4 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flammability Classification (1.50 mm) | HB | IEC 60695-11-10, -20 |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Melt Density | 1.00 | g/cm³ | |
| Specific Heat Capacity of Melt | 2100 | J/kg/°C | |
| Thermal Conductivity of Melt | 0.15 | W/m/K |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Effective Thermal Diffusivity | 0.0544 | cSt |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Synthos PS GP 585A | Synthos S.A. | PS (GPPS) | Synthos PS |
| WPP TPO TPO-277 P Black | Washington Penn Plastic Co. Inc. | TPO | WPP TPO |
| Colorite 66 Series 5066 | Colorite Polymers | PVC, Unspecified | Colorite 66 Series |
| Hapsil™ 360 | Hapco Inc. | Rubber | Hapsil™ |
| Implex® Implex | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Implex® |