ELEVATE™ EF446
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Westlake Chemical Corporation |
| Trademark: | ELEVATE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1fGV72_ELEVATE-EF446.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Westlake EF446 resin is a 6.0% EVA copolymer designed for general purpose packaging film. This Kosher compliant resin has excellent clarity, toughness, heat sealing characteristics, low temperature brittleness properties, and machinability. Application/Uses: High Clarity Packaging Foam Applications |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.925 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | 2.0 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 6.0 | wt% |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 32 | µm | |
| secant modulus 1 | ASTM D882 | ||
| 1% secant, MD : 32 µm, blown film | 109 | MPa | ASTM D882 |
| 1% secant, TD : 32 µm, blown film | 127 | MPa | ASTM D882 |
| Tensile Strength 2 | ASTM D882 | ||
| MD : Broken, 32 µm, blown film | 30.0 | MPa | ASTM D882 |
| TD : Broken, 32 µm, blown film | 26.0 | MPa | ASTM D882 |
| Tensile Elongation 3 | ASTM D882 | ||
| MD : Broken, 32 µm, blown film | 440 | % | ASTM D882 |
| TD : Broken, 32 µm, blown film | 770 | % | ASTM D882 |
| Dart Drop Impact 4(32 µm, Blown Film) | 180 | g | ASTM D1709A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss 5(45°, 31.8 µm, Blown Film) | 73 | ASTM D2457 | |
| Haze 6(31.8 µm, Blown Film) | 4.3 | % | ASTM D1003 |
| Additional Information |
|---|
| Test specimens for blown film: nominal thickness 1.25 mils; blow up ratio 2.5:1, die gap 35 mils. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 182 - 199 | °C |
| Extrusion instructions |
|---|
| Melt temperatures of 360° F - 390° F are recommended for Westlake Chemical EF446 with blow-up ratios of 1.5:1 or higher. |
| Note Message | |
|---|---|
| 1 . | Test run at 23°C (73°F) and 50% relative humidity |
| 2 . | Test run at 23°C (73°F) and 50% relative humidity |
| 3 . | Test run at 23°C (73°F) and 50% relative humidity |
| 4 . | Test run at 23°C (73°F) and 50% relative humidity |
| 5 . | Base Polymer |
| 6 . | Base Polymer |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ DP-9156-5-8000 | PolyOne Corporation | PP Homopolymer | Maxxam™ |
| Kemcor LD 4200 (INJECTION) | Qenos Pty Ltd | LDPE | Kemcor |
| Hyundai EP PA66 LD460Z | HYUNDAI EP Co., Ltd. | Nylon 66 | Hyundai EP PA66 |
| LITEN VB 85 | UNIPETROL RPA | PE Copolymer | LITEN |
| POFEX EP8300S 95M | POLYROCKS CHEMICAL CO., LTD | TPU, Unspecified | POFEX |