Borealis PE FA6220
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Borealis AG |
| Trademark: | Borealis PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1ehMsI_Borealis-PE-FA6220.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FA6220 is a Low Density Polyethylene for Film Extrusion. Autoclave Technology. Includes Antioxidant. This grade is developed for the production of thin blown films. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.1 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic) | 0.90 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Film Puncture Energy (40 µm) | 1.30 | J | ASTM D5748 |
| Secant Modulus | ASTM D882A | ||
| MD : 40 µm | 200 | MPa | |
| TD : 40 µm | 210 | MPa | |
| Tensile Strength | ISO 527-3 | ||
| MD : 40 µm | 26.0 | MPa | |
| TD : 40 µm | 20.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 40 µm | 350 | % | |
| TD : Break, 40 µm | 600 | % | |
| Dart Drop Impact (40 µm) | 100 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 40 µm | 5.0 | N | |
| TD : 40 µm | 3.0 | N |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 111 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (40.0 µm) | 85 | ASTM D2457 | |
| Haze (40.0 µm) | 7.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 to 180 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® LDC 710 | Marco Polo International, Inc. | LDPE | MARPOL® |
| MARPOL® HDM 509 | Marco Polo International, Inc. | HDPE | MARPOL® |
| Sevrene® 2000-60A | Vi-Chem Corporation | TPE | Sevrene® |
| TRILOY® 210GNH30 | Samyang Corporation | PC+ABS | TRILOY® |
| DAI-EL™ G-701 | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |