Ultrason® E 2010 G6
| Category: | PESU , Polyethersulfone |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultrason® E |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1dFf7s_Ultrason-E-2010-G6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultrason E 2010 G6 is a 30% glass reinforced, medium viscosity injection molding PESU grade with high rigidity and strength. Applications Typical applications include circuit braker parts, lamp holders, heat shields, impellers, and printer cartridges. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.59 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (360°C/10.0 kg) | 25.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.58 | % | |
| Flow | 0.28 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 1.6 | % | |
| Equilibrium, 23°C, 50% RH | 0.60 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 224 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 9800 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 150 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.3 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 8.0 | kJ/m² | |
| 23°C | 9.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | 60 | kJ/m² | |
| 23°C | 55 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180 | ||
| -30°C | 9.5 | kJ/m² | |
| 23°C | 10 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 223 | °C | ISO 75-2/A |
| CLTE - Flow | 1.5E-5 | cm/cm/°C | |
| RTI Elec | UL 746 | ||
| 1.60 mm | 180 | °C | |
| 3.00 mm | 180 | °C | |
| RTI Imp | UL 746 | ||
| 1.60 mm | 180 | °C | |
| 3.00 mm | 190 | °C | |
| RTI Str | UL 746 | ||
| 1.60 mm | 190 | °C | |
| 3.00 mm | 190 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 37 | kV/mm | IEC 60243-1 |
| Dielectric Constant | IEC 60250 | ||
| 100 Hz | 4.30 | ||
| 1 MHz | 4.30 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 2.0E-3 | ||
| 1 MHz | 0.010 | ||
| Comparative Tracking Index | 125 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 3.00 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 130 to 150 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 350 to 390 | °C | |
| Mold Temperature | 150 to 190 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Appeel® 22D843 | DuPont Packaging & Industrial Polymers | EA | Appeel® |
| ATTANE™ 4606G | The Dow Chemical Company | ULDPE | ATTANE™ |
| Grilon® BGZ-30 | EMS-GRIVORY | Nylon 6 | Grilon® |
| Kumho EPS SEPS N30 | Korea Kumho Petrochemical Co., Ltd. | PS (EPS) | Kumho EPS |
| Plaslube® PC / ABS 8001A | Techmer Engineered Solutions | PC+ABS | Plaslube® |