HiFill® PA6 GF30 IM HS L
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1cg6ct_HiFill-PA6-GF30-IM-HS-L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HiFill®PA6 GF30 IM HS L is a polyamide 6 (nylon 6) product that contains a glass fiber reinforced material. It can be processed by injection molding and is available in North America. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.33 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.10 | -- | % | ASTM D955 |
| Water Absorption (24 hr) | 1.5 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength (Break) | 145 | 100 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | 8.0 | % | ASTM D638 |
| Flexural Modulus | 8270 | 4830 | MPa | ASTM D790 |
| Flexural Strength | 234 | 165 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ASTM D256 | |||
| -40°C, 3.18 mm | 130 | -- | J/m | ASTM D256 |
| 23°C, 3.18 mm | 190 | 340 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 1400 J/m | No Break | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 210 | -- | °C | ASTM D648 |
| CLTE - Flow | 3.6E-5 | -- | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 2.0E+15 | -- | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 15 | -- | kV/mm | ASTM D149 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 266 - 277 | °C | |
| Middle Temperature | 277 - 288 | °C | |
| Front Temperature | 271 - 282 | °C | |
| Nozzle Temperature | 271 - 282 | °C | |
| Processing (Melt) Temp | 277 - 288 | °C | |
| Mold Temperature | 79.4 - 104 | °C | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.00 - 0.345 | MPa |
| Injection instructions |
|---|
| Screw Speed: MediumRecommendations for Molding and Tool Conditions: Well vented moldMoisture Content, as received: Product is packaged at 0.2% or less. |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1005 MS 2 | RTP Company | PBT | RTP |
| Unipren® Elastomers A3 CRLA010 35A EG06IN4 UP332 | Petropol Industry and Trade of Polymers LTDA | TPE | Unipren® Elastomers |
| Etinox® EF-0127 | Ercros, S.A. | PVC, Rigid | Etinox® |
| Petrothene® NA204000 (Extrusion Coating) | LyondellBasell Industries | LDPE | Petrothene® |
| Sylvin 4299-65 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |