Tenite™ Propionate 360E4861312 Clear, Trsp

Category:	CAP , Cellulose Acetate Propionate
Manufacturer:	Eastman Chemical Company
Trademark:	Tenite™ Propionate
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	1bCas7_Tenite-Propionate-360E4861312-Clear-Trsp.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Tenite™ cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm feel. The mechanical properties of Tenite™ cellulosic plastics differ with plasticizer levels. Lower plasticizer content yields a harder surface, higher heat resistance, greater rigidity, higher tensile strength, and better dimensional stability. Higher plasticizer content increases impact strength. Tenite™ cellulosic plastics are available in natural, clear, selected ambers or smoke transparents and black translucent. Color concentrates are available in let-down ratios from 10:1 to 40:1. Tenite™ Cellulosic Acetate Propionate 360-12 has a plasticizer level of 12%. It is resistant to high temperatures.

General Information
Additive	Plasticizer (12%)
Features	Durable Food Contact Acceptable Good Chemical Resistance Good Colorability Good Processability Good Strength Good Toughness High Clarity High Gloss High Hardness High Heat Resistance Plasticized Renewable Resource Content Soft
Uses	Cosmetic Packaging Eyeglass Frames Eyeglasses Medical/Healthcare Applications Personal Care Stationary Supplies Toothbrush Handles Writing Instruments
Agency Ratings	FDA Food Contact, Unspecified Rating
Appearance	Amber Black Clear/Transparent Natural Color
Forms	Pellets

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.20	g/cm³	ASTM D792
Molding Shrinkage - Flow	0.20 to 0.60	%	ASTM D955
Water Absorption (23°C, 24 hr)	1.5	%	ASTM D570

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (R-Scale, 23°C)	78		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength			ASTM D638
Yield, 23°C	31.7	MPa
Break, 23°C	33.1	MPa
Tensile Elongation (Break, 23°C)	45	%	ASTM D638
Flexural Modulus (23°C)	1450	MPa	ASTM D790
Flexural Strength (Yield, 23°C)	41.4	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact			ASTM D256
-40°C	110	J/m
23°C	420	J/m

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load ¹			ASTM D648
0.45 MPa, Annealed	83.0	°C
1.8 MPa, Annealed	75.0	°C
Vicat Softening Temperature ²	96.0	°C	ASTM D1525
CLTE - Flow (23°C)	2.0E-5	cm/cm/°C	ASTM D696
Specific Heat (23°C)	1260 to 1670	J/kg/°C	DSC
Thermal Conductivity ³(23°C)	0.25	W/m/K	ASTM C177

Electrical	Nominal Value	Unit	Test Method
Dielectric Strength (23°C)	12 to 19	kV/mm	ASTM D149
Dielectric Constant (23°C, 1 MHz)	3.30 to 3.80		ASTM D150
Dissipation Factor (23°C, 1 MHz)	0.010 to 0.15		ASTM D150

Optical	Nominal Value	Unit	Test Method
Refractive Index	1.460 to 1.490		ASTM D542
Transmittance (1520 µm)	> 90.0	%	ASTM D1003
Haze (1520 µm)	< 8.5	%	ASTM D1003

Additional Information	Nominal Value	Unit	Test Method
Soluble Matter Loss (23°C)	0.10	%	ASTM D570
Weight Loss on Heating - 72 hrs (80°C)	0.40	%	ASTM D1562

Note Message
1 .	Conditioned 4 hours at 70°C (158°F)
2 .	Conditioned 4 hours at 70°C (158°F)
3 .	Range: 0.17 to 0.33

Resin Grade	Manufacturer	Category	Trademark
MarFlex® 1017	Chevron Phillips Chemical Company LLC	LDPE	MarFlex®
NILFLEX® SH A80 MC009	Taro Plast S.p.A.	SEBS	NILFLEX®
Exac PFA	Saint Gobain - Norton	PFA	Exac
Hostacom G2 N01	LyondellBasell Industries	PP Homopolymer	Hostacom