DENKA ABS QF
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Denka Company Limited |
| Trademark: | DENKA ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1a92Mi_DENKA-ABS-QF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DENKA ABS QF is an Acrylonitrile Butadiene Styrene (ABS) product. It is available in Asia Pacific, Europe, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.04 | g/cm³ | ASTM D792 |
| 23°C | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 44 | g/10 min | ISO 1133 |
| Molding Shrinkage (2.00 mm) | 0.40 to 0.60 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 113 | ASTM D785 | |
| R-Scale | 110 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 43.0 | MPa | ASTM D638 |
| -- | 2400 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 45.0 | MPa | |
| Break | 34.0 | MPa | |
| Nominal Tensile Strain at Break | 28 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 2 | 2400 | MPa | ASTM D790 |
| -- 3 | 2350 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 4 | 70.0 | MPa | ASTM D790 |
| -- 5 | 72.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 19 | kJ/m² | ISO 179 |
| Notched Izod Impact | 200 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed 6 | 86.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 75.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 99.0 | °C | ASTM D1525 7 |
| -- | 97.0 | °C | ISO 306/B |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 8 | > 1.0E+16 | ohms | JIS K6911 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 85.0 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Rear Temperature | 170 to 190 | °C | |
| Middle Temperature | 180 to 215 | °C | |
| Front Temperature | 190 to 230 | °C | |
| Nozzle Temperature | 190 to 225 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Back Pressure | 0.490 to 0.981 | MPa | |
| Screw Speed | 80 to 120 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 15 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 15 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | Edgewise |
| 7 . | Loading 2 (50 N) |
| 8 . | 23°C, 50% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Unichem 4196 | Colorite Polymers | PVC, Unspecified | Unichem |
| Hostaform® C 9021 AW XAP² ™ LS | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Plexiglas® 7N | Evonik Industries AG | Acrylic (PMMA) | Plexiglas® |
| Polifil® Nylon 638L | The Plastics Group | Nylon 66 | Polifil® Nylon |
| Sylvin 8225-55 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |