LNP™ THERMOCOMP™ ZX06323 compound
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1ZFOGq_LNP-THERMOCOMP-ZX06323-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| This material is mineral filled PPO grade with high dielectric constant and low loss tangent |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.95 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/5.0 kg) | 8.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.64 | % | |
| Across Flow : 24 hr | 0.56 | % | |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4140 | MPa | ASTM D638 |
| -- | 4090 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 54.0 | MPa | ASTM D638 |
| Break | 54.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 4.2 | % | ASTM D638 |
| Break | 4.7 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 3940 | MPa | ASTM D790 |
| -- 5 | 4390 | MPa | ISO 178 |
| Flexural Strength 6 | ASTM D790 | ||
| Yield, 50.0 mm Span | 102 | MPa | |
| Break, 50.0 mm Span | 102 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 47 | J/m | ASTM D256 |
| 23°C 7 | 5.4 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 290 | J/m | ASTM D4812 |
| 23°C 8 | 21 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 122 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 9 | 123 | °C | ISO 75-2/Af |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant 10(0.900 GHz) | 6.40 | ASTM D2520 | |
| Dissipation Factor (0.900 GHz) | 3.0E-3 | ASTM D150 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 105 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Rear Temperature | 280 to 285 | °C | |
| Middle Temperature | 290 to 295 | °C | |
| Front Temperature | 300 to 305 | °C | |
| Nozzle Temperature | 290 to 295 | °C | |
| Processing (Melt) Temp | 295 to 305 | °C | |
| Mold Temperature | 90.0 | °C | |
| Back Pressure | 9.00 | MPa | |
| Screw Speed | 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | Method B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8627-45 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| VECTRA® A515 | Celanese Corporation | LCP | VECTRA® |
| Clariant Nylon 6 PA-213XO12 | Clariant Corporation | Nylon 6 | Clariant Nylon 6 |
| POLLITE 1002G30 | POLYROCKS CHEMICAL CO., LTD | PC | POLLITE |
| LEXAN™ EXL4016H resin | SABIC Innovative Plastics | PC | LEXAN™ |