STYRON A-TECH™ 1290
| Category: | PS (GPPS) , General Purpose Polystyrene |
| Manufacturer: | Americas Styrenics LLC |
| Trademark: | STYRON A-TECH™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1Z8DzX_STYRON-A-TECH-1290.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
STYRON A- TECH™1290 is a general-purpose polystyrene material,. This product is available in Latin America and is processed by extrusion, thermoforming or injection molding. STYRON A- TECH™The main features of the 1290 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 3.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 - 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ASTM D638 |
| Tensile Strength (Break) | 23.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 40 | % | ASTM D638 |
| Flexural Modulus | 2120 | MPa | ASTM D790 |
| Flexural Strength | 35.0 | MPa | ASTM D790 |
| Tensile Rupture | 25.0 | MPa | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 23°C | 180 | J/m | ASTM D256 |
| 23°C, molded | 95 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 94.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 86.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 103 | °C | ASTM D1525 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 199 - 213 | °C | |
| Middle Temperature | 218 - 249 | °C | |
| Front Temperature | 218 - 249 | °C | |
| Nozzle Temperature | 213 - 243 | °C | |
| Back Pressure | 0.200 - 1.20 | MPa |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 177 - 193 | °C | |
| Cylinder Zone 2 Temp. | 182 - 204 | °C | |
| Cylinder Zone 3 Temp. | 188 - 210 | °C | |
| Cylinder Zone 4 Temp. | 199 - 216 | °C | |
| Cylinder Zone 5 Temp. | 204 - 221 | °C | |
| Adapter Temperature | 193 - 232 | °C | |
| Melt Temperature | 193 - 232 | °C | |
| Die Temperature | 199 - 232 | °C |
| Extrusion instructions |
|---|
| Polish Rolls: 66 - 104 °CHead Pressure: 10 - 21 MPA |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3564 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| TEREZ PA 10.10 7500 GF 30 ECO | TER HELL PLASTIC GMBH | Nylon 1010 | TEREZ PA 10.10 |
| Novalloy-B B2704 | PlastxWorld Inc. | ABS+PBT | Novalloy-B |
| Fluoraz 799 | Greene, Tweed & Co. | PTFE | Fluoraz |
| POLIMAXX 2440TC | IRPC Public Company Limited | PP Impact Copolymer | POLIMAXX |